半結晶性ポリピロール:フィルタ紙の細孔を通して合成したポリスチレンスルホン酸塩【JST・京大機械翻訳】

Semi-crystalline polypyrrole: Polystyrene sulfonate synthesized through the pores of filter paper

著者 (7件)： Kang Kyung Seok (Department of Polymer Science and Engineering, Pusan National University, Busan, South Korea) ,  Jee Chanhyuk (Department of Polymer Science and Engineering, Pusan National University, Busan, South Korea) ,  Bae Ji-Hong (Department of Polymer Science and Engineering, Pusan National University, Busan, South Korea) ,  Kim Eunyoung (Department of Polymer Science and Engineering, Pusan National University, Busan, South Korea) ,  Jung Hyo Jin (Department of Polymer Science and Engineering, Pusan National University, Busan, South Korea) ,  Yang Jung Yup (Department of Physics, Kunsan National University, Gunsan, South Korea) ,  Huh PilHo (Department of Polymer Science and Engineering, Pusan National University, Busan, South Korea)
資料名： Polymer Engineering & Science  (Polymer Engineering & Science)
巻： 58  号： 7  ページ： 1033-1036  発行年： 2018年 
JST資料番号： C0640A  ISSN： 0032-3888  CODEN： PYESA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 半結晶性ポリピロール:ポリスチレンスルホン酸塩(PPy:PSS)複合材料を,濾紙のミクロ細孔を通過させた後に,首尾よく合成した。フィルタ紙をトンネルとして用いて,開始剤の拡散速度をチャンネル化し,占有細孔容積の関数としてPSS鎖を分離した。Fourier変換赤外分光法(FT-IR)は,形成されたPPy:PSSの特異的結合構造を示唆した。PPy:PSS複合材料の結晶構造を,用いた濾紙の種々の細孔サイズに基づくX線回折により解析した。伝導率の結晶度依存性を標準4点プローブを用いて評価した。異なる結晶性を有する一連のPPy:PSS試料は,0.007S/cmから0.062S/cmの範囲の電気伝導率を示した。Copyright 2018 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 細孔径 ,  チャネル ,  *フィルタ ,  X線回折 ,  濾紙 ,  複合材料 ,  *ポリピロール ,  重合開始剤 ,  電気伝導率 ,  *細孔 ,  結晶構造 ,  拡散速度 ,  プローブ ,  結晶度
準シソーラス用語： 細孔容積 , 【Automatic Indexing@JST】