メタけい酸ナトリウムの存在下でのMgO SiO_2スラリーの水和反応の発達【Powered by NICT】

Hydration evolution of MgO-SiO₂ slurries in the presence of sodium metasilicate

著者 (5件)： Zhang Yu (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, PR China) ,  Li Yawei (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, PR China) ,  Dai Yajie (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, PR China) ,  Liu Jun (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, PR China) ,  Xu Yibiao (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 44  号： 6  ページ： 6626-6633  発行年： 2018年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： マグネシウム-silicate-水和物ゲル(M S H)の形成を促進するためには,メタケイ酸ナトリウムはMgO SiO_2スラリーに添加した。MgO SiO_2スラリーの水和過程に及ぼすメタケイ酸ナトリウムの効果を本研究において調べた。M-S-Hの形成を容易にし,ブルーサイトの生成を抑制するために比較的少量のメタケイ酸ナトリウムを必要とした。初期24時間で,M S Hは溶液中のマグネシウムイオンとケイ酸塩種の高濃度のために急速に形成した。硬化時間の更なる増加と共に,M S Hゲル相は連続的に成長した。さらに,十分なケイ酸塩イオン量はM-S-H相に新たに形成されたブルーサイトの変換に有利であった。メタけい酸ナトリウムの添加は反応過程のみならず水和物の形態に影響した。卵黄-殻構造の代わりに,花状および積層シート状M-S-Hはメタケイ酸ナトリウムの存在下で形成された。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 卵黄 ,  *酸化マグネシウム ,  ブルーサイト ,  *水和 ,  水和物 ,  ゲル ,  *スラリー ,  高速度 ,  *水和反応 ,  イオン ,  ケイ酸塩
準シソーラス用語： 反応過程 ,  硬化時間 ,  マグネシウムイオン ,  *メタケイ酸ナトリウム , 【Automatic Indexing@JST】

著者キーワード (4件)： マグネシウム-silicate-水和物 ,  反応過程 ,  Morphology ,  硬化時間

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (5件)： メタけい酸ナトリウム ,  MgO ,  スラリー ,  水和反応 ,  発達