新規CoCrFeNiTa_x共晶高エントロピー合金の微細構造と性質【Powered by NICT】

Microstructure and properties of novel CoCrFeNiTa_x eutectic high-entropy alloys

著者 (8件)： Huo Wenyi (Jiangsu Key Laboratory of Advanced Metallic Materials, Southeast University, Nanjing, 211189, China) ,  Zhou Hui (Jiangsu Key Laboratory of Advanced Metallic Materials, Southeast University, Nanjing, 211189, China) ,  Fang Feng (Jiangsu Key Laboratory of Advanced Metallic Materials, Southeast University, Nanjing, 211189, China) ,  Zhou Xuefeng (Jiangsu Key Laboratory of Advanced Metallic Materials, Southeast University, Nanjing, 211189, China) ,  Xie Zonghan (School of Mechanical Engineering, University of Adelaide, SA, 5005, Australia) ,  Xie Zonghan (School of Engineering, Edith Cowan University, WA, 6027, Australia) ,  Jiang Jianqing (Jiangsu Key Laboratory of Advanced Metallic Materials, Southeast University, Nanjing, 211189, China) ,  Jiang Jianqing (Nanjing Forestry University, Nanjing, 210037, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 735  ページ： 897-904  発行年： 2018年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 共晶高エントロピー合金は構造用合金の潜在的な置換物質,それらの微細構造と性質に起因した。本研究では,CoCrFeNiTa_x(モル比xが0.1,0.2,0.3,0.395,0.4と0.5,x値)共晶高エントロピー合金をアーク融解法で作製した。二相,FCC固溶体とLaves相は,合金において同定した。合金はTa含有量の増加と共に亜共晶から過共晶凝固した。CoCrFeNiTa_0 0.395共晶高エントロピー合金は1.4GPaの超高降伏強度を示すが,CoCrFeNiTa_0 3亜共晶高エントロピー合金は2.5GPaの圧縮強さと44%の破壊歪を示した。そのような顕著な強化効果は第二相強化,固溶体強化と境界強化間の理想的な組合せに起因することを示した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 凝固 ,  モル比 ,  圧縮強さ ,  アーク融解 ,  固溶体 ,  *微細構造 ,  *タンタル ,  降伏強さ ,  Laves相 ,  第二相 ,  *合金 ,  *共晶
準シソーラス用語： 破壊歪 ,  過共晶 ,  *高エントロピー合金 , 【Automatic Indexing@JST】

著者キーワード (4件)： 高エントロピー合金 ,  Laves相 ,  共晶 ,  タンタル

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： 共晶 ,  高エントロピー合金 ,  微細構造 ,  性質