構造-相状態及び銅イオンで処理したVT1-0チタン合金の表面層の微小硬さ【Powered by NICT】

The structure - phase state and microhardness of the surface layer of the VT1-0 titanium alloys treated by copper ions

著者 (9件)： Fedorischeva M.V. (Institute of Strength Physics and Materials Science, SB RAS, Russia, Tomsk, 634055, Russia) ,  Fedorischeva M.V. (Tomsk Polytechnic University, Russia, Tomsk, 634050, Russia) ,  Kalashnikov M.P. (Institute of Strength Physics and Materials Science, SB RAS, Russia, Tomsk, 634055, Russia) ,  Kalashnikov M.P. (Tomsk Polytechnic University, Russia, Tomsk, 634050, Russia) ,  Nikonenko A.V. (National Research Tomsk State University, Russia, Tomsk, 634050, Russia) ,  Bozhko I.A. (Institute of Strength Physics and Materials Science, SB RAS, Russia, Tomsk, 634055, Russia) ,  Bozhko I.A. (Tomsk Polytechnic University, Russia, Tomsk, 634050, Russia) ,  Sergeev V.P. (Institute of Strength Physics and Materials Science, SB RAS, Russia, Tomsk, 634055, Russia) ,  Sergeev V.P. (Tomsk Polytechnic University, Russia, Tomsk, 634050, Russia)
資料名： Vacuum  (Vacuum)
巻： 149  ページ： 150-155  発行年： 2018年 
JST資料番号： E0347A  ISSN： 0042-207X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 相組成,構造と~0.5~2.5keVのエネルギーをもつ銅イオンによって改質されたVT1-0チタンの表面とイオン電流密度~2...20mA~2の形態をX線回折,SEMおよびTEMにより調べた。銅イオンによるVT10チタンの処理時の表面層におけるCu-Ti平衡状態図の金属間相であることを確立した。断面の改質表面層は,処理時間に依存して1μmまでと1μm4.5 5.0μmまでの厚さの二層に分割した。二準位マイクロとナノ細孔ナノ結晶構造は改質層に形成される。相構造とVT1-0合金の表面層の形態は,処理時間に依存することが分かった。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： X線回折 ,  相組成 ,  *チタン合金 ,  *微小硬さ ,  イオン電流 ,  *表層 ,  *合金 ,  加工時間
準シソーラス用語： 相構造 ,  ナノ結晶構造 ,  ナノ細孔 ,  二層 ,  平衡状態図 ,  *銅イオン , 【Automatic Indexing@JST】

著者キーワード (5件)： 構造-相状態 ,  チタン ,  事情 ,  改質 ,  微小硬さ

分類 (4件)： 気相めっき  (WC08022K) ,  金属の機械的性質  (BL01022T) ,  電極過程  (CB07040U) ,  酸化物薄膜  (BK14050P)

タイトルに関連する用語 (4件)： 銅イオン ,  チタン合金 ,  表面層 ,  微小硬さ