炭素熱還元と組み合わせた水熱蒸着により作製したC/C ZrC複合材料の微細構造と性質【Powered by NICT】

Microstructure and properties of C/C-ZrC composites prepared by hydrothermal deposition combined with carbothermal reduction

著者 (5件)： Li Cuiyan (School of Materials Science & Engineering, Shaanxi University of Science & Technology, Xi’an, Shaanxi, 710021, China) ,  Li Guibiao (School of Materials Science & Engineering, Shaanxi University of Science & Technology, Xi’an, Shaanxi, 710021, China) ,  Ouyang Haibo (School of Materials Science & Engineering, Shaanxi University of Science & Technology, Xi’an, Shaanxi, 710021, China) ,  Huang Jianfeng (School of Materials Science & Engineering, Shaanxi University of Science & Technology, Xi’an, Shaanxi, 710021, China) ,  Hou Xianghui (Faculty of Engineering, The University of Nottingham, Nottingham, NG7 2RD, UK)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 741  ページ： 323-330  発行年： 2018年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ZrC(C/C ZrC)複合材料を含む炭素繊維強化炭素マトリックスは炭素熱還元と組み合わせた水熱堆積により作製した。サブミクロンZrC粒子(100 300 nm)は,マトリックス中に分散した。複合材料の応力-歪曲線は典型的な擬塑性破壊挙動を示した。複合材料の重量および線形アブレーション速度は3.7×10~ 3g/sおよび4.2×10~ 3mm/sであった。ZrO_2ガラス層の形成がアブレーションの中心に複合材料のエロージョンを減少させた。ZrCの酸化から発生した連続C ZrC ZrO_2骨格層はアブレーション縁領域でのエロージョンから複合材料を保護することができる。得られたC/C-ZrC複合材は,アブレージョン抵抗材料として有望な可能性を示した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *炭素 ,  *還元 ,  応力歪曲線 ,  *真空蒸着 ,  アブレーション ,  塑性 ,  *複合材料 ,  炭素繊維 ,  *微細構造 ,  線形性
準シソーラス用語： アブレージョン ,  エロージョン ,  破壊挙動 ,  *炭素熱還元 , 【Automatic Indexing@JST】

著者キーワード (4件)： C/C ZrC複合材料 ,  水熱堆積 ,  Microstructure ,  アブレーション抵抗

分類 (3件)： セラミック・磁器の性質  (YC03030G) ,  セラミック・陶磁器の製造  (YC03020V) ,  非金属材料へのセラミック被覆  (YC02040K)

タイトルに関連する用語 (7件)： 炭素熱還元 ,  水 ,  熱蒸着 ,  作製 ,  複合材料 ,  微細構造 ,  性質