熱機械パルプ繊維で強化されたバイオポリエチレン:機械的およびマイクロ機械的特性化と溶融堆積モデリングによる3D印刷におけるその応用【JST・京大機械翻訳】

Bio-polyethylene reinforced with thermomechanical pulp fibers: Mechanical and micromechanical characterization and its application in 3D-printing by fused deposition modelling

著者 (6件)： Tarres Q. (LEPAMAP Group, Department of Chemical Engineering, University of Girona, Girona, 17071, Spain) ,  Melbo J.K. (RISE PFI, Trondheim, NO-7491, Norway) ,  Delgado-Aguilar M. (LEPAMAP Group, Department of Chemical Engineering, University of Girona, Girona, 17071, Spain) ,  Espinach F.X. (Design, Development and Product Innovation, Dept. of Organization, Business, University of Girona, Girona, 17071, Spain) ,  Mutje P. (LEPAMAP Group, Department of Chemical Engineering, University of Girona, Girona, 17071, Spain) ,  Chinga-Carrasco G. (RISE PFI, Trondheim, NO-7491, Norway)
資料名： Composites. Part B. Engineering  (Composites. Part B. Engineering)
巻： 153  ページ： 70-77  発行年： 2018年 
JST資料番号： W0437B  ISSN： 1359-8368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： バイオ複合材料を製造するために,2つのバイオベースポリエチレン(BioPE)と熱機械パルプ(TMP)繊維を用いた。機械的性質に及ぼすTMP繊維の影響を詳細に評価した。溶融バイオ複合材料の粘度の増加を定量化し,TMP繊維(0~30%w/w)の取り込みに関連した。機械的性質に及ぼす無水マレイン酸(MAPE)で官能化したポリエチレンの影響を定量した。純粋なBioPEsと比較して,6%w/wのMAPEと30%w/wのTMP繊維を含むバイオ複合材料に対して,115と127%の間の引張強さの最大の増加が得られた。10および20%TMP繊維を含む配合バイオ複合材料は,溶融堆積モデリングにより三次元(3D)印刷された。TMP繊維は3D印刷を促進し,それに応じてバイオ複合材料の機械的性質を改善することを確認した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *モデリング ,  *機械パルプ ,  引張強さ ,  三次元 ,  *印刷 ,  粘度 ,  *ポリエチレン ,  機械的性質 ,  官能化
準シソーラス用語： バイオ複合材料 ,  *三次元印刷 ,  *パルプ繊維 , 【Automatic Indexing@JST】

著者キーワード (5件)： 天然繊維 ,  バイオ複合材料 ,  バイオポリエチレン ,  機械的性質 ,  3D印刷