新規な超分岐ポリシロキサン改質剤を用いた同時強化と強靭化エポキシ網目【Powered by NICT】

Simultaneously reinforcing and toughening epoxy network with a novel hyperbranched polysiloxane modifier

著者 (4件)： Liu Hanchao (State Key Laboratory of Polymer Material Engineering, College of Polymer Science and Engineering, Sichuan University, Chengdu, 610065, China) ,  Gao Xiaoxiao (State Key Laboratory of Polymer Material Engineering, College of Polymer Science and Engineering, Sichuan University, Chengdu, 610065, China) ,  Deng Bo (State Key Laboratory of Polymer Material Engineering, College of Polymer Science and Engineering, Sichuan University, Chengdu, 610065, China) ,  Huang Guangsu (State Key Laboratory of Polymer Material Engineering, College of Polymer Science and Engineering, Sichuan University, Chengdu, 610065, China)
資料名： Journal of Applied Polymer Science  (Journal of Applied Polymer Science)
巻： 135  号： 23  ページ： ROMBUNNO.46340  発行年： 2018年 
JST資料番号： C0467A  ISSN： 0021-8995  CODEN： JAPNAB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 新規な超分岐ポリシロキサン(HBPSi)を調製し,硬化相分離を用いないエポキシ芳香族アミンネットワークに入れた。HBPSiの中程度の含有量は,HBPSi上の活性アミノ基のために,架橋ネットワークの架橋密度を増加させた。一方,HBPSi分子上の第二アミンはエポキシネットワークの均一性を改善した。5wt%HBPSi含有量では,引張強さ,引張弾性率,曲げ弾性率は,純エポキシ樹脂のそれらと比較して,それぞれ,17.6%,13.7%,および17.5%向上した。一方,破断伸びおよび衝撃強度は,純エポキシ樹脂のそれらよりも63.3%および49.1%高かった。HBPSiも有意に材料のチャー収率を増加させ,熱重量損失速度を減少させた;これは改善された熱安定性を示した。Copyright 2018 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 第二アミン ,  衝撃強さ ,  引張強さ ,  相分離 ,  重量損失 ,  *ネットワーク ,  架橋度 ,  熱安定性 ,  チャー
準シソーラス用語： 破断伸び ,  曲げ弾性係数 ,  引張弾性係数 ,  *強靱化 , 【Automatic Indexing@JST】

著者キーワード (6件)： デンドリマ ,  ガラス転移 ,  超分岐重合体と大環状化合物 ,  機械的性質 ,  構造性質の関係 ,  熱硬化性樹脂

分類 (2件)： 難燃剤  (YH05060Q) ,  その他の高分子の反応  (CG03040H)

タイトルに関連する用語 (5件)： 分岐 ,  ポリシロキサン ,  改質剤 ,  強化 ,  強靭化