La_2-xCa_xNiO_4+δにおける表面欠陥化学と酸素交換動力学【JST・京大機械翻訳】

Surface defect chemistry and oxygen exchange kinetics in La_2-x Ca _x NiO_4+δ

著者 (14件)： Tropin E.S. (Institute of High Temperature Electrochemistry, UB RAS, Laboratory of Solid State Oxide Fuel Cells, Yekaterinburg 620137, Russia) ,  Tropin E.S. (Ural Federal University named after the First President of Russia B.N. Yeltsin, Department of Chemical Engineering, Yekaterinburg 620002, Russia) ,  Ananyev M.V. (Institute of High Temperature Electrochemistry, UB RAS, Laboratory of Solid State Oxide Fuel Cells, Yekaterinburg 620137, Russia) ,  Ananyev M.V. (Ural Federal University named after the First President of Russia B.N. Yeltsin, Department of Chemical Engineering, Yekaterinburg 620002, Russia) ,  Farlenkov A.S. (Institute of High Temperature Electrochemistry, UB RAS, Laboratory of Solid State Oxide Fuel Cells, Yekaterinburg 620137, Russia) ,  Farlenkov A.S. (Ural Federal University named after the First President of Russia B.N. Yeltsin, Department of Chemical Engineering, Yekaterinburg 620002, Russia) ,  Khodimchuk A.V. (Institute of High Temperature Electrochemistry, UB RAS, Laboratory of Solid State Oxide Fuel Cells, Yekaterinburg 620137, Russia) ,  Khodimchuk A.V. (Ural Federal University named after the First President of Russia B.N. Yeltsin, Department of Chemical Engineering, Yekaterinburg 620002, Russia) ,  Berenov A.V. (Imperial College London, Department of Materials, London, Great Britain, UK) ,  Fetisov A.V. (Institute of Metallurgy, Laboratory of Statics and Kinetics of Processes, UB RAS, Yekaterinburg 620049, Russia) ,  Eremin V.A. (Institute of High Temperature Electrochemistry, UB RAS, Laboratory of Solid State Oxide Fuel Cells, Yekaterinburg 620137, Russia) ,  Eremin V.A. (Ural Federal University named after the First President of Russia B.N. Yeltsin, Department of Chemical Engineering, Yekaterinburg 620002, Russia) ,  Kolchugin A.A. (Institute of High Temperature Electrochemistry, UB RAS, Laboratory of Solid State Oxide Fuel Cells, Yekaterinburg 620137, Russia) ,  Kolchugin A.A. (Ural Federal University named after the First President of Russia B.N. Yeltsin, Department of Chemical Engineering, Yekaterinburg 620002, Russia)
資料名： Journal of Solid State Chemistry  (Journal of Solid State Chemistry)
巻： 262  ページ： 199-213  発行年： 2018年 
JST資料番号： H0505A  ISSN： 0022-4596  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： La_2-xCa_xNiO_4+δ(x=0;0.1;0.3)における表面酸素交換動力学と拡散を,600~800°Cの温度範囲と0.13~2.5kPaの酸素圧力範囲における気相平衡による同位体交換法によって研究した。La_2-xCa_x NiO_4+δの電気伝導率の増強にもかかわらず,酸素表面交換(k*)と酸素トレーサ拡散(D*)係数はLa_2NiO_4+δと比較して有意に低かった。酸素交換の基本段階の速度を計算した。Caドーピングにより,律速段階の変化が観察された。最近開発されたモデルによると,酸化物の表面は酸素交換過程に対して不均一であることが分かった。このような不均一性の理由を,表面欠陥化学および酸素表面交換および拡散率に及ぼすCaの影響と同様に考察した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 酸化物 ,  同位体交換 ,  不均一性 ,  拡散係数 ,  電気伝導率 ,  律速 ,  *酸素 ,  相平衡 ,  *カルシウム ,  ドーピング ,  *表面欠陥
準シソーラス用語： トレーサ拡散 ,  酸素分圧 ,  温度範囲 , 【Automatic Indexing@JST】

著者キーワード (5件)： ランタンカルシウムニッケル酸塩 ,  LEIS ,  XPS ,  EBSD ,  希土類金属偏析

分類 (1件)： 塩基,金属酸化物  (CD01030Z)