電場下でのセメントモルタル中のTSAに及ぼす温度の影響【Powered by NICT】

Effect of temperatures on TSA in cement mortars under electrical field

著者 (6件)： Zeng Qianpu (College of Materials Science and Engineering, Chongqing University, 400045 Chongqing, China) ,  Wang Chong (College of Materials Science and Engineering, Chongqing University, 400045 Chongqing, China) ,  Luo Yaoling (College of Materials Science and Engineering, Chongqing University, 400045 Chongqing, China) ,  Yu Chao (China Merchants Chongqing Communications Technology Research & Design Institute, 400067 Chongqing, China) ,  Huang Qian (School of Civil and Architectural Engineering, Yangtze Normal University, 408100 Chongqing, China) ,  Luo Chaoqun (College of Materials Science and Engineering, Chongqing University, 400045 Chongqing, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 162  ページ： 88-95  発行年： 2018年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,電場下でのセメントモルタルの硫酸塩腐食のサウマサイト形(TSA)に及ぼす温度の影響を調べることを目的とした。モルタルを 5°C,5°C,20°C,5°C-20°Cサイクルで保存されていた。損傷を視覚的に観察し,試験片の圧縮強度を定期的に試験した。X線回折(XRD)とFourier変換赤外分光法(FTIR)は,劣化生成物を分析するために実施した。結果は150日後に完全浸せきと電気の両方の下で20°Cで試料がほとんど損傷を受けた及びソーマス石は検出できないことを示した。 5°Cで試験片の破壊は主に凍結融解および塩スケーリング,得られた表面損傷によるものであった。さらに,電場は,モルタルにおける硫酸塩作用により誘起された損傷を促進し,5°Cでの試料の劣化したTSAの形成に主として起因していた。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： FTIR分光法 ,  X線回折 ,  硫酸塩 ,  浸漬 ,  *セメントモルタル ,  視覚 ,  凍結融解 ,  腐食 ,  圧縮強さ ,  *モルタル ,  *電場
準シソーラス用語： 表面損傷 ,  ソーマス石 , 【Automatic Indexing@JST】

著者キーワード (4件)： 温度 ,  ソーマス石 ,  電場 ,  硫酸塩攻撃

分類 (1件)： モルタル,コンクリート  (RA06042H)

タイトルに関連する用語 (3件)： 電場 ,  セメントモルタル ,  TSA