Al_2O_3-SiO_2系におけるゲル-ガラス転移の解明【JST・京大機械翻訳】

Clarifying the gel-to-glass transformation in Al₂O₃-SiO₂ systems

著者 (7件)： Liu Shujiang (School of Materials Science and Engineering, Qilu University of Technology (Shandong Academy of Sciences), Jinan 250353, China) ,  Boffa Vittorio (Department of Chemistry and Bioscience, Aalborg University, 9220 Aalborg, Denmark) ,  Yang Dongliang (Shandong Guiyuan Advanced Ceramic Co., Ltd., Zibo, China) ,  Fan Zhenkun (Shandong Guiyuan Advanced Ceramic Co., Ltd., Zibo, China) ,  Meng Fanpeng (Shandong Guiyuan Advanced Ceramic Co., Ltd., Zibo, China) ,  Yue Yuanzheng (School of Materials Science and Engineering, Qilu University of Technology (Shandong Academy of Sciences), Jinan 250353, China) ,  Yue Yuanzheng (Department of Chemistry and Bioscience, Aalborg University, 9220 Aalborg, Denmark)
資料名： Journal of Non-Crystalline Solids  (Journal of Non-Crystalline Solids)
巻： 492  ページ： 77-83  発行年： 2018年 
JST資料番号： D0642A  ISSN： 0022-3093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本論文では,示差走査熱量測定,X線回折,赤外(IR)分光法および透過型電子顕微鏡法により,ゾル-ゲル誘導xAl_2O_3-(100-x)SiO_2(x=0,10,20および30mol)系のゲル-ガラス(G-G)変態挙動を明らかにした。SiO_2-Al_2O_3ゲルは,純粋なSiO_2参照ゲルより低いG-G転移温度を示した。SiO_2ゲルへのAl_2O_3の添加は,ヒドロキシル濃度に及ぼすガラス転移温度(T_g)の依存性を抑制することができ,この効果はアルミナ-シリカゲル中の高度に架橋した構造に起因する。さらに,Alリッチ相はSiリッチマトリックス相から分離し,そのような非混和性はAl_2O_3含有量の増加と共に増加した。この挙動は溶融急冷アルミナ-シリカガラスのそれと類似している。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  *ガラス ,  ガラス転移点 ,  石英ガラス ,  急冷 ,  *ゲル ,  アルミニウム ,  赤外線 ,  シリカゲル ,  *ガラス転移 ,  アルミナ ,  示差走査熱量測定 ,  ゾル-ゲル法
準シソーラス用語： 非混和性 ,  *一酸化ケイ素 ,  透過型電子顕微鏡法 , 【Automatic Indexing@JST】

著者キーワード (4件)： SiO_2-Al_2O_3ゲル ,  ゲルからガラスへの変換 ,  ガラス転移 ,  不混和性

分類 (2件)： ガラスの性質・分析・試験  (YC02030Z) ,  塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (2件)： ゲル ,  ガラス転移