固体酸化物燃料電池のためのナノファイバーに基づくLa_0 4Sr_0 6TiO_3Gd_0 2Ce_0 8O_1 9-Ni複合アノード【Powered by NICT】

Nanofiber-based La_0.4Sr_0.6TiO ₃-Gd_0.2Ce_0.8O_1.9-Ni composite anode for solid oxide fuel cells

著者 (5件)： Hu Qianjun (School of Chemical Engineering and Technology, Harbin Institute of Technology, 92 West Dazhi Street, Harbin 150001, China) ,  Liu Chaojun (School of Chemical Engineering and Technology, Harbin Institute of Technology, 92 West Dazhi Street, Harbin 150001, China) ,  Fan Liquan (College of Materials Science and Engineering, Qiqihar University, No.42, Wenhua Street, Qiqihar 161006, China) ,  Wang Yuwei (College of Materials Science and Engineering, Qiqihar University, No.42, Wenhua Street, Qiqihar 161006, China) ,  Xiong Yueping (School of Chemical Engineering and Technology, Harbin Institute of Technology, 92 West Dazhi Street, Harbin 150001, China)
資料名： Electrochimica Acta  (Electrochimica Acta)
巻： 265  ページ： 1-9  発行年： 2018年 
JST資料番号： B0535B  ISSN： 0013-4686  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： La_0 4Sr_0 6TiO_3(LST)ナノ繊維を電界紡糸法により調製した,LSTナノ繊維足場は,YSZ(8mo1%Y_2O_3 92mo1%ZrO_2)電解質フレーク上に焼結し,Gd_0 2Ce_0 8O_1(GDC)とNiはLa_0 4Sr_0 6TiO_3ナノ繊維足場に浸潤する。本論文では,ナノファイバーベースのLST GDC Ni複合材料アノードであるH_2またはCH_4燃料ガスで試験し,優れた熱安定性と酸化還元サイクル安定性を示した。炭素沈着はCH_4燃料ガスを供給した100後にナノファイバーベースのLST GDC Ni複合材料アノードの表面に現れる。炭素析出の量はNi:LSTの質量比に比例した。少量のカーボン析出が電気化学的性能を向上させるが,大量のカーボン析出が反対であった。LST:GDC:Niの最適質量比は1:1:0.4であることが分かった。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： フレーク ,  酸化還元反応 ,  炭素 ,  焼結 ,  *ナノファイバ ,  熱安定性 ,  複合材料 ,  *ニッケル ,  *固体酸化物燃料電池 ,  *アノード ,  エレクトロスピニング ,  気体燃料
準シソーラス用語： 電気化学的性能 ,  質量比 ,  サイクル安定性 , 【Automatic Indexing@JST】

著者キーワード (5件)： La_0 4Sr_0 6TiO_3 ,  Gd_0 2Ce_0 8O_1 9 ,  Ni ,  安定性 ,  炭素蒸着

分類 (2件)： 燃料電池  (YB04040V) ,  電気化学反応  (CB07050F)

タイトルに関連する用語 (4件)： 固体酸化物燃料電池 ,  ナノファイバー ,  Ni ,  アノード