フェライト系ステンレス鋼上のMnに富む保護酸化物スケールの生成に及ぼす(FeCrSi)_2(MoNb)型Laves相の役割【Powered by NICT】

The role of (FeCrSi)₂(MoNb)-type Laves phase on the formation of Mn-rich protective oxide scale on ferritic stainless steel

著者 (6件)： Ali-Loytty Harri (Surface Science Group, Laboratory of Photonics, Tampere University of Technology, P.O. Box 692, FI-33101 Tampere, Finland) ,  Hannula Markku (Surface Science Group, Laboratory of Photonics, Tampere University of Technology, P.O. Box 692, FI-33101 Tampere, Finland) ,  Juuti Timo (Centre for Advanced Steels Research, University of Oulu, P.O.B. 4200, FI-90014 Oulu, Finland) ,  Niu Yuran (MAX IV Laboratory, Lund University, P.O. Box 118, SE-22100 Lund, Sweden) ,  Zakharov Alexei A. (MAX IV Laboratory, Lund University, P.O. Box 118, SE-22100 Lund, Sweden) ,  Valden Mika (Surface Science Group, Laboratory of Photonics, Tampere University of Technology, P.O. Box 692, FI-33101 Tampere, Finland)
資料名： Corrosion Science  (Corrosion Science)
巻： 132  ページ： 214-222  発行年： 2018年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 反応性元素を用いたステンレス鋼のマイクロアロイングは耐酸化性を増加させるが,合金微細構造変化を容易にする。XPSの結果は,650°Cで120hの熱処理後のTi-Nb安定化フェライト系ステンレス鋼(EN 1.4521)の初期酸化機構の変化を明らかにする(FeCrSi)2(MoNb)型Laves相の時効析出は微量合金元素の顕著な表面偏析と酸化をもたらした。Siは他のスケール形成元素の外方拡散成形拡散障壁によるLaves析出物位置で優先的に酸化する。最も重要なことはMnの拡散と表面での低揮発性(Mn,Cr)3O_4スピネル酸化物の形成は強く抑制された。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *酸化 ,  *ケイ素 ,  *マンガン ,  耐酸化性 ,  *酸化物 ,  表面偏析 ,  *ステンレス鋼 ,  *酸化膜 ,  析出物 ,  熱処理 ,  合金 ,  *Laves相 ,  合金元素 ,  拡散障壁
準シソーラス用語： *フェライト系ステンレス鋼 , 【Automatic Indexing@JST】

著者キーワード (5件)： A.ステンレス鋼 ,  B XPS ,  Cインタフェイス ,  C偏析 ,  C酸化

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (6件)： フェライト系ステンレス鋼 ,  Mn ,  酸化物スケール ,  型 ,  Laves相 ,  役割