両性ナノ粒子の凍結乾燥後のを誘導する長期コロイド安定性と安定性への静電的媒介後官能化の実現可能性【Powered by NICT】

Feasibility of Electrostatic-Mediated Post-Functionalization to Induce Long Term Colloidal Stability and Stability After Freeze Drying of Amphoteric Nanoparticles

著者 (4件)： Yeap Swee Pin (Department of Chemical & Petroleum Engineering, Faculty of Engineering, Technology & Built Environment, UCSI University, Cheras, Kuala Lumpur 56000, Malaysia.) ,  Lim JitKang (School of Chemical Engineering, Universiti Sains Malaysia, Nibong Tebal, Penang 14300, Malaysia.) ,  Ooi Boon Seng (School of Chemical Engineering, Universiti Sains Malaysia, Nibong Tebal, Penang 14300, Malaysia.) ,  Ahmad Abdul Latif (School of Chemical Engineering, Universiti Sains Malaysia, Nibong Tebal, Penang 14300, Malaysia.)
資料名： Colloid and Interface Science Communications  (Colloid and Interface Science Communications)
巻： 23  ページ： 14-20  発行年： 2018年 
JST資料番号： W3024A  ISSN： 2215-0382  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 市販酸化鉄ナノ粒子(両性的性質)を単純な静電仲介後官能化法によるポリ(ナトリウム4-スチレンスルホナート)で表面改質した(PSS)。鉄酸化物ナノ粒子は,表面特性の完全な変化を受けるかどうか修飾に成功した。官能化はpH=3.5で実施したとき,そのような観察が得られ,鉄酸化物ナノ粒子とPSS分子は逆の電荷であった。ここでPSSは静電引力を介して酸化鉄上に付着することができた。とは対照的に,官能化はpH>9で実行したときに,貧弱な表面改質をした,酸化鉄とPSSは同様な表面電荷を持つに互いに反発する。その後,長期間(6カ月)のための酸化鉄ナノ粒子の良好なコロイド安定性と凍結乾燥プロセスから維持する能力を継続的に静電仲介後官能化の能力は,粒子流体力学的サイズの進化を追跡することにより評価した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 表面性状 ,  表面電荷 ,  表面改質 ,  *官能化 ,  *ナノ粒子 ,  酸化鉄 ,  *凍結乾燥 ,  流体力学
準シソーラス用語： 酸化鉄ナノ粒子 ,  *コロイド安定性 , 【Automatic Indexing@JST】

著者キーワード (6件)： 静電 ,  Functionalization ,  Nanoparticles ,  両性 ,  Stabilization ,  凍結乾燥

分類 (3件)： 塩基,金属酸化物  (CD01030Z) ,  酸化物結晶の磁性  (BM06050E) ,  医用素材  (GA05040H)

タイトルに関連する用語 (8件)： ナノ粒子 ,  凍結乾燥 ,  誘導 ,  長期 ,  コロイド安定性 ,  安定性 ,  官能化 ,  実現可能性