Bearing strength and failure behavior of pinned hybrid glass-flax composite laminates

著者 (5件)： Fiore V. (Department of “Civil, Environmental, Aerospace and Materials Engineering”, University of Palermo, Viale delle Scienze, Edificio 6, 90128 Palermo, Italy) ,  Calabrese L. (Department of Engineering, University of Messina, Contrada Di Dio (Sant’Agata), 98166 Messina, Italy) ,  Scalici T. (Department of “Civil, Environmental, Aerospace and Materials Engineering”, University of Palermo, Viale delle Scienze, Edificio 6, 90128 Palermo, Italy) ,  Bruzzaniti P. (Department of Engineering, University of Messina, Contrada Di Dio (Sant’Agata), 98166 Messina, Italy) ,  Valenza A. (Department of “Civil, Environmental, Aerospace and Materials Engineering”, University of Palermo, Viale delle Scienze, Edificio 6, 90128 Palermo, Italy)
資料名： Polymer Testing  (Polymer Testing)
巻： 69  ページ： 310-319  発行年： 2018年 
JST資料番号： C0752B  ISSN： 0142-9418  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究の目的は,亜麻/エポキシ積層材料のピンホール強度に及ぼすガラス織物の外部層の影響を評価することである。積層順序に依存する固定継手性能を評価するために,単一重ね軸受試験を行った。ハイブリッド積層材料の機械的挙動をより良く同定するために,完全ガラスと亜麻積層材料も比較した。特に,軸受応力と破壊機構を,継手形状を変えて調べた。さらに,ピン止めハイブリッド複合材料積層材料の主要な破壊モードをクラスタ化する実験的破壊マップを用いて,継手の機械的破壊と幾何学的パラメータの間の関係をより良く明らかにした。実験結果は,亜麻/エポキシ積層材料におけるガラス布の外部層の存在が機械的に固定された継手の機械的性能に正の影響を及ぼすことを示した。さらに,ハイブリッド積層材料において,ベアリング破壊機構は,広範囲の継手形状に対して生じ,従って,亜麻ベース複合材料積層材料の接合設計を支持した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： クラスタ化 ,  形態 ,  *ガラス ,  ハイブリッド複合材料 ,  *軸受 ,  *積層材料 ,  破壊モード ,  ピンホール ,  複合材料 ,  *ピン止め ,  接合
準シソーラス用語： ガラスクロス ,  破壊機構 ,  *破壊挙動 , 【Automatic Indexing@JST】

著者キーワード (6件)： 軸受 ,  ハイブリッドラミネート ,  ガラス ,  アマ ,  故障モード ,  機械的継手

分類 (2件)： 機械的性質  (YH02022L) ,  ゴム・プラスチック材料  (HC04030W)

タイトルに関連する用語 (6件)： ピン止め ,  ガラス ,  亜麻 ,  積層材 ,  軸受 ,  破壊挙動