Ag-Cu-Tiろう材でろう付したBN Si_3N_4及びAlON継手のミクロ組織と機械的性質【Powered by NICT】

Microstructure and mechanical properties of BN-Si₃N₄ and AlON joints brazed with Ag-Cu-Ti filler alloy

著者 (6件)： Liu Mingxu (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China) ,  Liu C.F. (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China) ,  Zhang J. (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China) ,  Tao Rui (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China) ,  Zhang Qiang (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China) ,  Qi Qin (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China)
資料名： Journal of the European Ceramic Society  (Journal of the European Ceramic Society)
巻： 38  号： 4  ページ： 1265-1270  発行年： 2018年 
JST資料番号： E0801B  ISSN： 0955-2219  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： AlONはAg-Cu-Tiフィラー合金を用いたBN Si_3N_4にろう付けすることに成功した。SEM,TEMおよびXRD研究は,TiN+TiB_2+Ti_5Si_3反応層はBN Si_3N_4に隣接して生成したAlONに隣接して形成される(Cu,Al)3Ti_3O層であることを明らかにした。添加では,Ag-Cu共晶,Cu(s,s)とAlCu_2Tiはろう材で観察された。継手のミクロ組織と機械的性質に及ぼすろう付温度の影響を調べた。ろう付け温度が増加するにつれて,反応層は厚くなったが,ろう付シームの厚さは減少した。一方,量とAlCu_2Ti金属間化合物のサイズは減少した。継手のせん断強さは最初増加し,その後,ろう付温度の上昇と共に低下した。は850°Cで15分間ロウ付けされた場合,94MPaの最大強度を持つ継手が得られた。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 剪断強さ ,  *機械的性質 ,  充填材料 ,  *ろう付 ,  共晶 ,  合金 ,  金属間化合物 ,  X線回折 ,  *ろう材
準シソーラス用語： ピーク強度 , 【Automatic Indexing@JST】

著者キーワード (4件)： BN Si_3N_4 ,  AlON ,  ろう付 ,  Ag-Cu-Ti充填材

分類 (2件)： ろう付  (WC07050C) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (9件)： Ag ,  Cu ,  Ti ,  ろう材 ,  ろう付 ,  BN ,  継手 ,  ミクロ組織 ,  機械的性質