2219アルミニウム合金のミクロ組織と腐食挙動に及ぼす予変形の影響【JST・京大機械翻訳】

Effects of pre-deformation on the microstructures and corrosion behavior of 2219 aluminum alloys

著者 (7件)： Lu Yalin (Key Construction Laboratory of Green Forming and Equipment from Jiangsu Province, China) ,  Lu Yalin (School of Materials Engineering, Jiangsu University of Technology, Changzhou, China) ,  Wang Jian (School of Materials Engineering, Jiangsu University of Technology, Changzhou, China) ,  Li Xingcheng (School of Materials Engineering, Jiangsu University of Technology, Changzhou, China) ,  Li Wen (Key Construction Laboratory of Green Forming and Equipment from Jiangsu Province, China) ,  Li Ruolin (School of Materials Engineering, Jiangsu University of Technology, Changzhou, China) ,  Zhou Dongshuai (Key Construction Laboratory of Green Forming and Equipment from Jiangsu Province, China)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 723  ページ： 204-211  発行年： 2018年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,2219アルミニウム合金のミクロ組織と腐食挙動に及ぼす異なる予変形の影響を調べた。その結果,結晶粒のサイズは徐々に減少し,析出相の分布は時効処理中に効果的に改善され,引張強さと耐食性の明らかな増加をもたらすことを示した。それは,θ′析出相に対する優先条件を与える予変形過程によって誘起された大量の転位を示した。20%の予変形を受けたこの合金に対する微細で分散したθ′相は,引張強さを強化する転位の運動を効果的に妨げた。予変形が30%に達すると,引張強さはθ′相の不均一分布のためにわずかに減少した。最高から最低への時効処理後の異なる予変形の耐食性のランクは,20%>30%>10%>5%のように引き出すことができ,θ′析出物の母集団の変化と析出自由域(PFZ)の幅に起因した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 母集団 ,  析出物 ,  *合金 ,  耐食性 ,  引張強さ ,  結晶粒 ,  *アルミニウム合金
準シソーラス用語： 不均一分布 ,  *腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： 2219アルミニウム合金 ,  前変形 ,  微細構造 ,  機械的性質 ,  腐食挙動