強弾性SmNb_1-xTa_xO_4セラミックの合成と熱物理特性【JST・京大機械翻訳】

Synthesis and thermophysics properties of ferroelastic SmNb_1-XTa_XO₄ ceramics

著者 (5件)： Luo Yinyi (Faculty of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, People’s Republic of China) ,  Chen Lin (Faculty of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, People’s Republic of China) ,  Wu Peng (Faculty of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, People’s Republic of China) ,  Song Peng (Faculty of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, People’s Republic of China) ,  Feng Jing (Faculty of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, People’s Republic of China)
資料名： Ceramics International  (Ceramics International)
巻： 44  号： 12  ページ： 13999-14006  発行年： 2018年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 単斜晶相SmNb_1-XTa_XO_4セラミックを固相反応により合成した。X線回折とRamanスペクトルを適用して結晶構造を特性化した。SmNb_1-XTa_XO_4セラミックの強弾性を,走査電子顕微鏡によって観察されたドメイン構造によって確認した。SmNb_1-XTa_XO_4セラミックのバンドギャップは4.3から5.0eVの範囲であり,それらはUV光に対して優れた吸収を示した。SmNb_1-XTa_XO_4セラミックの比熱,熱拡散率,熱伝導率および熱膨張係数を含む熱物理特性を系統的に調べた。その結果,SmNb_1-XTa_XO_4セラミックの熱伝導率は1.33Wm~-1K~-1(900°C)と低く,熱膨張係数は11.7×10~-6K~-1(1200°C)と高いことを示した。独特の強弾性と優れた熱物理特性は,SmNb_1-XTa_XO_4セラミックが有望な遮熱被覆材料であることを示す。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 遮熱コーティング ,  結晶構造 ,  X線回折 ,  走査電子顕微鏡 ,  温度伝導率 ,  単斜晶系 ,  バンドギャップ ,  熱伝導率 ,  キャラクタリゼーション ,  *セラミック ,  熱膨張係数 ,  Ramanスペクトル ,  *強弾性 ,  微細構造 ,  固相反応

著者キーワード (5件)： 遮熱コーティング材料 ,  微細構造 ,  強弾性 ,  熱膨張係数 ,  熱伝導率

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (3件)： 強弾性 ,  セラミック ,  物理特性