SUS430鋼相互接続上の電着Ni/CeO_2多層被覆【JST・京大機械翻訳】

Electrodeposited Ni/CeO₂ mulriple coating on SUS 430 steel interconnect

著者 (4件)： Li Yandong (School of Metallurgy, Liaoning Key Laboratory for Metallurgical Sensor and Technology, Northeastern University, 3-11 Wenhua Road, Shenyang, 110819, China) ,  Li Yandong (Key Laboratory of Extraordinary Bond Engineering and Advanced Materials Technology of Chongqing, Yangtze Normal University, Chongqing 408100, China) ,  Geng Shujiang (School of Metallurgy, Liaoning Key Laboratory for Metallurgical Sensor and Technology, Northeastern University, 3-11 Wenhua Road, Shenyang, 110819, China) ,  Chen Gang (School of Metallurgy, Liaoning Key Laboratory for Metallurgical Sensor and Technology, Northeastern University, 3-11 Wenhua Road, Shenyang, 110819, China)
資料名： International Journal of Hydrogen Energy  (International Journal of Hydrogen Energy)
巻： 43  号： 28  ページ： 12811-12816  発行年： 2018年 
JST資料番号： B0192B  ISSN： 0360-3199  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Ni/CeO_2多重被覆を,電着法によりSUS430鋼上に作製した。800°Cにおける空気への100時間の初期および3週間の長期熱暴露は,Ni/CeO_2被覆鋼上に成長した酸化物スケールがNiFe_2O_4スピネルの外部酸化物層,NiOの中間酸化物層およびCr_2O_3の内部酸化物層を含むことを示した。同時に,分散CeO_2粒子は酸化物スケールに埋め込まれた。不連続CeO_2粒子を含まない同じ三層酸化物構造が同じ曝露環境で成長するNi被覆鋼と比較して,Ni/CeO_2被覆鋼上の内部Cr_2O_3層の成長速度は大いに抑制され,その後,酸化物スケール面積比抵抗(ASR)を低下させた。酸化抵抗の増強と酸化物スケールASRの減少はCeO_2の存在に起因する。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *被覆 ,  成長速度 ,  固体酸化物燃料電池 ,  酸化物 ,  スピネル ,  *鋼 ,  *電着 ,  電気抵抗率 ,  被覆鋼材 ,  *ニッケル ,  不連続性 ,  酸化膜 ,  酸化層 ,  酸化 ,  耐酸化性

著者キーワード (5件)： 共電着 ,  Ni/CeO_2 ,  固体酸化物燃料電池の相互接続 ,  酸化 ,  面積比抵抗