その場超音波測定によるGdドープLaCrO_3等原子価の構造転移【Powered by NICT】

Structural transition in Gd doped LaCrO₃ isovalent by in-situ ultrasonic measurements

著者 (6件)： Thamilmaran P. (Department of Physics, Sri SRNM College, Sattur 626 203, Tamil Nadu, India) ,  Arunachalam M. (Department of Physics, Sri SRNM College, Sattur 626 203, Tamil Nadu, India) ,  Sankarrajan S. (Department of Physics, Sethu Institute of Technology, Kariapatti 626 115, Tamil Nadu, India) ,  Sakthipandi K. (Department of Physics, Sethu Institute of Technology, Kariapatti 626 115, Tamil Nadu, India) ,  Sivabharathy M. (Department of Physics, Sethu Institute of Technology, Kariapatti 626 115, Tamil Nadu, India) ,  Jebaseelan Samuel E. James (Department of Physics, School of Advanced Sciences, VIT University, Vellore 632 014, Tamil Nadu, India)
資料名： Physica B. Condensed Matter  (Physica B. Condensed Matter)
巻： 530  ページ： 270-276  発行年： 2018年 
JST資料番号： H0676B  ISSN： 0921-4526  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ガドリニウム置換LaCrO_3等原子価ペロブスカイトを本研究で調べた。La_1 xGd_xCrO_3(x=0~0,0.025,0.05,0.10,0.15および0.20)の試料を固相反応法を用いて調製した。X線回折(XRD)パターンは,作製した試料は室温でPnma空間群を持つ斜方晶構造を持つことを確認した。試料の結晶サイズは組成xが0,0.025,0.05,0.10,0.15と0.20のそれぞれ98 89 76 72 60および55nmであり,同じことが試料中のGdの置換の増加と共に減少する。試料の走査電子顕微鏡画像は,それぞれ組成xが0,0.025,0.05,0.10,0.15と0.20の150%,131%,129%,120%,116および94nmの粒子サイズの球状のような形態を有していた。その場超音波測定は構造転移を決定するために,300~700Kの広い温度範囲で行った。測定された温度依存性の超音波パラメータは高温で調製した試料の菱面体晶相から斜方晶への構造相転移を調査するために使用した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 三方晶系 ,  斜方晶系 ,  固相反応 ,  X線回折 ,  温度依存性 ,  *構造相転移 ,  粒度 ,  *超音波応用計測 ,  *ガドリニウム ,  空間群 ,  *超音波 ,  *ドーピング ,  高温 ,  *原子価
準シソーラス用語： SEM画像 , 【Automatic Indexing@JST】

著者キーワード (4件)： ランタンクロム鉄鉱 ,  超音波速度 ,  減衰 ,  構造転移

分類 (2件)： 固相転移  (BL04020G) ,  金属酸化物及び金属カルコゲン化物の結晶構造  (BK07020Y)

タイトルに関連する用語 (5件)： 超音波測定 ,  Gd ,  ドープ ,  原子価 ,  構造転移