周期的Niバッファ層を用いたL1_0型FeCo秩序構造の作製【JST・京大機械翻訳】

Fabrication of L1₀-type FeCo ordered structure using a periodic Ni buffer layer

著者 (7件)： Ito Hisaaki (Tokyo University of Science, 6-3-1, Niijuku, Katsushika, Tokyo 125-8585, Japan) ,  Saito Masahiro (Tokyo University of Science, 6-3-1, Niijuku, Katsushika, Tokyo 125-8585, Japan) ,  Miyamachi Toshio (The Institute for Solid State Physics, The University of Tokyo, 5-1-5 Kashiwanoha, Kashiwa, Chiba 277-8581, Japan) ,  Komori Fumio (The Institute for Solid State Physics, The University of Tokyo, 5-1-5 Kashiwanoha, Kashiwa, Chiba 277-8581, Japan) ,  Koganezawa Tomoyuki (Japan Synchrotron Radiation Research Institute (JASRI/SPring-8), 1-1-1 Koto, Sayo, Hyogo 679-5198, Japan) ,  Mizuguchi Masaki (Institute for Materials Research, Tohoku University, 2-1-1 Katahira, Aoba, Sendai 980-8577, Japan) ,  Kotsugi Masato (Tokyo University of Science, 6-3-1, Niijuku, Katsushika, Tokyo 125-8585, Japan)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 9  号： 4  ページ： 045307-045307-5  発行年： 2019年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 著者らは,B2構造転移を抑制し,L1_0構造を維持するために,周期的バッファ層を挿入することによって,L1_0-FeCo秩序構造を有する強磁性体を実験的に調製した。試料はパルスレーザ蒸着(PLD)を用いた交互単原子層の堆積を含む技術を用いて作製した。この技術を用いて,CuまたはNiをバッファ層として用いた(7ML-FeCo/3ML-バッファ)_3薄膜を堆積した。RHEED,AFM,SR-XRD,およびSQUIDにより,試料の表面粗さ,表面形態,格子構造,および磁気特性をそれぞれ特性化した。その結果,周期的Niバッファ層を有するL1_0-FeCo超構造の構築を初めて確認した。CuをNiで置換することにより,磁気モーメントと磁気異方性の両方も増加した。Copyright 2019 AIP Publishing LLC All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 構造相転移 ,  *ニッケル ,  格子構造 ,  *バッファ層 ,  銅 ,  X線回折 ,  磁気異方性 ,  磁気モーメント ,  パルスレーザ蒸着 ,  単原子層 ,  キャラクタリゼーション ,  強磁性体
準シソーラス用語： 超構造 ,  表面形態 ,  *秩序構造 , 【Automatic Indexing@JST】

分類 (5件)： その他の無機化合物の磁性  (BM06060P) ,  金属薄膜  (BK14030T) ,  その他の接合  (BM03088W) ,  磁電デバイス  (NC03100X) ,  金属結晶の磁性  (BM06040T)

タイトルに関連する用語 (4件)： Ni ,  バッファ層 ,  秩序構造 ,  作製