単端切欠き引張試験片を用いたAPI X90高級パイプライン鋼の溶接継手の破壊靱性に関する実験的研究【JST・京大機械翻訳】

Experimental Study on the Fracture Toughness of Welded Joints of API X90 High-grade Pipeline Steels Using Single-Edge-Notched Tension Specimens

著者 (5件)： Kong Lingzhen (School of Oil and Natural Gas Engineering, Southwest Petroleum University, Sichuan, China) ,  Zhou Xiayi (State Key Laboratory of Oil and Gas Reservoir Geology and Exploitation, Southwest Petroleum University, Sichuan, China) ,  Chen Liqiong (School of Oil and Natural Gas Engineering, Southwest Petroleum University, Sichuan, China) ,  Huang Kun (School of Oil and Natural Gas Engineering, Southwest Petroleum University, Sichuan, China) ,  Chen Jie (School of Oil and Natural Gas Engineering, Southwest Petroleum University, Sichuan, China)
資料名： Arabian Journal for Science and Engineering  (Arabian Journal for Science and Engineering)
巻： 44  号： 2  ページ： 1033-1041  発行年： 2019年 
JST資料番号： W4051A  ISSN： 2193-567X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： API X90パイプライン鋼の溶接継手の破壊靭性とR曲線を実験的に研究した。単一エッジ切欠き引張(SENT)試験片と正規化法を採用した。3つの技術(A,B,C)を用いて溶接した継手を調べた。結果は,SENT試料が溶接継手の破壊靭性とR曲線を試験するために使用できることを示している。溶接法Bの溶接継手は最も劣った破壊靭性を示した。そして,熱影響部のR曲線および破壊靱性は,溶接部および母材によって,著しく影響を受けた。熱影響部の破壊靭性とR曲線を試験する新しいアイデアも提案した。Copyright 2018 King Fahd University of Petroleum & Minerals Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *パイプライン用鋼 ,  *切欠き ,  溶接 ,  *破壊靱性 ,  *溶接継手 ,  *引張 ,  *引張試験 ,  正規化 ,  溶接部

著者キーワード (5件)： X90 ,  高級パイプライン ,  SENT ,  溶接継手 ,  破壊靱性