2180Kまでの加熱黒鉛と銅粒子を用いた黒鉛分散銅複合材料の調製【JST・京大機械翻訳】

Preparation of graphite-dispersed copper composite with heating graphite and copper particles to 2180 K

著者 (6件)： Yokoyama S. (Department of Mechanical Engineering, Toyohashi University of Technology, Tempaku-cho, Toyohashi, Aichi, 441-8580, Japan) ,  Ishikawa Y. (Department of Mechanical Engineering, Graduate School of Toyohashi University of Technology, Tempaku-cho, Toyohashi, Aichi, 441-8580, Japan) ,  Baharuddin M. U. A. (Department of Mechanical Engineering, Graduate School of Toyohashi University of Technology, Tempaku-cho, Toyohashi, Aichi, 441-8580, Japan) ,  Hisyamudin M. N. N. (Department of Materials & Design Engineering, Universiti Tun Hussein Onn Malaysia Malaysia, Parit Raja, Batu Pahat, Johor, 86400 Malaysia) ,  Nishiyama K. (Department of Mechanical Engineering, NIT, Sasebo College, Sasebo, Japan) ,  Sasano J. (Department of Mechanical Engineering, Toyohashi University of Technology, Tempaku-cho, Toyohashi, Aichi, 441-8580, Japan)
資料名： AIP Conference Proceedings  (AIP Conference Proceedings)
巻： 2067  号： 1  ページ： 020007-020007-9  発行年： 2019年 
JST資料番号： D0071C  ISSN： 0094-243X  資料種別： 会議録 (C)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究では,グラファイト分散銅複合材料のバルクを調製することを試みた。黒鉛と銅粒子混合物をプレスすることにより調製したコンパクトを,誘導炉中で2173Kまで加熱した。アルゴンの大気圧下で調製した複合材料の場合,複合材料は多孔質であった。見掛け気孔率は,初期炭素含有量の増加に伴い,約10%から約50%に増加した。複合材料を真空中で約1500Kに加熱し,アルゴンの大気圧下で指定温度に加熱した場合,複合材料は緻密であった。見掛け気孔率は,初期炭素含有量の増加に伴い,約2%から約14%に増加した。電気抵抗は0.025Ωの下限と同じであり,複合材料の調製条件にかかわらず,電気抵抗は同じであった。2173Kで調製した複合材料の銅マトリックスの微小Vickers硬度は,初期炭素含有量に関係なく約0.5MPaであった。Copyright 2019 AIP Publishing LLC All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *グラファイト ,  多孔性 ,  多孔質体 ,  アルゴン ,  *複合材料 ,  *銅 ,  誘導炉 ,  Vickers硬さ ,  見掛気孔率