新規アルミノケイ酸塩YNi-5の合成と合成後処理による骨格熱安定性の増強【JST・京大機械翻訳】

Synthesis of novel aluminosilicate YNU-5 and enhancement of the framework thermal stability by post-synthesis treatment

著者 (4件)： Nakazawa Naoto (Division of Materials Science and Chemical Engineering, Yokohama National University, 79-5 Tokiwadai, Hodogaya-ku, Yokohama, 240-8501, Japan) ,  Yoshida Yuka (Division of Materials Science and Chemical Engineering, Yokohama National University, 79-5 Tokiwadai, Hodogaya-ku, Yokohama, 240-8501, Japan) ,  Inagaki Satoshi (Division of Materials Science and Chemical Engineering, Yokohama National University, 79-5 Tokiwadai, Hodogaya-ku, Yokohama, 240-8501, Japan) ,  Kubota Yoshihiro (Division of Materials Science and Chemical Engineering, Yokohama National University, 79-5 Tokiwadai, Hodogaya-ku, Yokohama, 240-8501, Japan)
資料名： Microporous and Mesoporous Materials  (Microporous and Mesoporous Materials)
巻： 280  ページ： 66-74  発行年： 2019年 
JST資料番号： E0642C  ISSN： 1387-1811  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 高濃度ケイ酸塩溶液から出発する高シリカゼオライトの非従来型水熱合成を調べた。結果として,12-8-環細孔系と孤立した8-環直線チャネルを含む新規ゼオライトYNU-5(YFI)を,有機構造指向剤として最も単純なテトラアルキルアンモニウム化合物の1つであるジメチルジプロピルアンモニウムを用いて合成した。MCM-68(MSE),ZSM-5(MFI)及びベータ(*BEA)のようないくつかの競合相が研究中に観察されたが,YNU-5(YFI)は狭い合成窓内の純粋相として得られた。硝酸を用いたポスト合成処理による脱アルミニウム挙動を研究し,YNU-5のSi/Alモル比を,酸濃度および/または温度を調整することにより,9~>200の範囲で制御した。フレームワークの熱安定性は,より厳しい酸処理条件下で強化され,安定化された材料はより良い触媒性能を示した。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： アルミニウム ,  触媒活性 ,  ケイ素 ,  モル比 ,  水熱合成 ,  *後処理 ,  細孔 ,  酸処理 ,  硝酸 ,  *アルミノケイ酸塩 ,  チャネル ,  *熱安定性 ,  *ケイ酸塩
準シソーラス用語： 脱アルミニウム ,  構造誘導剤 , 【Automatic Indexing@JST】

著者キーワード (4件)： YNi-5ゼオライト ,  ゼオライト合成 ,  脱アルミニウム ,  フレームワーク安定化

分類 (3件)： 合成鉱物  (CD01040K) ,  不均一系触媒反応  (CB06100E) ,  その他の触媒  (CB06123Z)

タイトルに関連する用語 (4件)： アルミノケイ酸塩 ,  骨格 ,  熱安定性 ,  増強