固体Feと液体Zn-6Al-3Mg合金の界面におけるFe-Al金属間化合物相の形成順序【JST・京大機械翻訳】

Formation sequence of Fe-Al intermetallic phases at interface between solid Fe and liquid Zn-6Al-3Mg alloy

著者 (4件)： Yokoi Hiroki (Department of Materials Process Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya, 464-8603, Japan) ,  Takata Naoki (Department of Materials Process Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya, 464-8603, Japan) ,  Suzuki Asuka (Department of Materials Process Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya, 464-8603, Japan) ,  Kobashi Makoto (Department of Materials Process Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya, 464-8603, Japan)
資料名： Intermetallics  (Intermetallics)
巻： 109  ページ： 74-84  発行年： 2019年 
JST資料番号： W0672A  ISSN： 0966-9795  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,異なる温度(400,460および500°C)および浸漬時間(2~3600s)でZn-6Al-3Mg(wt.%)合金融液中に熱間浸漬した格子間フリー(IF)鋼中に形成されたFe-Al金属間化合物相を特性化した。化学組成分析は,2秒の浸漬後でさえ,Zn合金融液へのFeの溶解を示した。微細構造特性化は,連続θ-Fe_4Al_13相層の初期形成を明らかにし,続いて,熱間浸漬過程の間の鋼とZn合金溶融側の両方に対するη-Fe_2Al_5相の局所成長が続いた。長期間の熱間浸漬後に,η相のさらなる成長は,Zn合金融液へのFeの著しい溶解を伴い,IF鋼板の厚さの損失をもたらした。全体として,著者らはFe-Al金属間化合物相の形成機構とZn-Al-Mg-Fe四元状態図の観点から固体Feと液体Zn合金の間の界面におけるそれらの関連成長を合理化し,文献で利用可能な熱力学データベースに従って計算した。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： η相 ,  浸漬 ,  鋼 ,  状態図 ,  *合金 ,  亜鉛合金 ,  *界面 ,  *鉄 ,  *マグネシウム合金 ,  *金属間化合物 ,  化学組成 ,  キャラクタリゼーション ,  微細構造 ,  被覆
準シソーラス用語： 融液 , 【Automatic Indexing@JST】

著者キーワード (5件)： 亜鉛めっき鋼 ,  Zn-Al-Mg合金被覆 ,  界面反応 ,  熱力学計算 ,  Fe_2Al_5相