応力腐食割れ機構に及ぼす高強度パイプライン鋼の熱影響部におけるミクロ組織的側面の影響:パートI.酸性土壌環境における【JST・京大機械翻訳】

Effect of microstructural aspects in the heat-affected zone of high strength pipeline steels on the stress corrosion cracking mechanism: Part I. In acidic soil environment

著者 (6件)： Li Xueda (School of Materials Science and Engineering, China University of Petroleum (East China), Qingdao, China) ,  Liu Jiahang (School of Materials Science and Engineering, China University of Petroleum (East China), Qingdao, China) ,  Sun Jianbo (School of Materials Science and Engineering, China University of Petroleum (East China), Qingdao, China) ,  Lin Xueqiang (School of Materials Science and Engineering, China University of Petroleum (East China), Qingdao, China) ,  Li Chunyu (School of Materials Science and Engineering, China University of Petroleum (East China), Qingdao, China) ,  Cao Ning (School of Materials Science and Engineering, China University of Petroleum (East China), Qingdao, China)
資料名： Corrosion Science  (Corrosion Science)
巻： 160  ページ： Null  発行年： 2019年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： X100パイプライン鋼の熱影響部におけるベイナイト/フェライトマトリックスとマルテンサイト-オーステナイト(M-A)成分の変化分布から成る微細構造をシミュレーションし,酸性土壌環境における応力腐食割れ(SCC)機構に及ぼすそれらの影響を研究した。結果は,微細構造特性,特にM-A成分の分布がSCC感受性に及ぼす大きな影響を持つことを示した。マイクロガルバニ効果,応力/歪濃度および水素関与は,M-A/マトリックス界面における微小ボイドの形成を促進し,微小ボイド合体によるSCC微小亀裂の開始および伝播を促進することができた。SCC微小亀裂は,上部ベイナイトラスに沿って伝搬するのを優先したが,針状フェライトと準多角形フェライトは,亀裂伝搬を抑制することができた。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面 ,  マルテンサイト ,  低合金鋼 ,  *パイプライン用鋼 ,  亀裂伝搬 ,  *金属組織 ,  感受性 ,  *応力腐食 ,  *応力腐食割れ ,  オーステナイト ,  微小亀裂 ,  ベイナイト ,  微細構造 ,  アシキュラーフェライト ,  *高強度 ,  *組織 ,  *亀裂 ,  *腐食割れ

著者キーワード (5件)： 低合金鋼 ,  酸性溶液 ,  B:SEM ,  C 応力腐食 ,  C:溶接

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (8件)： 応力腐食割れ ,  高強度 ,  パイプライン鋼 ,  熱影響部 ,  ミクロ組織 ,  パート ,  酸性 ,  土壌環境