低品質燃料中のCu-Ni-Sn-C-P焼結合金の耐食性に及ぼすNi含有量の影響【JST・京大機械翻訳】

The Influence of Ni Content on the Corrosion Resistance of Cu-Ni-Sn-C-P Sintered Alloys in Poor Quality Fuel

著者 (7件)： Sunada Satoshi (University of Toyama, Graduate School of Science and Engineering for Research, Toyama, Japan) ,  Mizukoshi Yusuke (University of Toyama (UT), Graduate School of Science and Engineering for Education, Toyama, Japan) ,  Sakagami Riku (Kyoto Institute of Technology, Department of Mechanical and System Engineering, Kyoto, Japan) ,  Takezoe Shinichi (Diamet Corporation (DM), Niigata, Japan) ,  Ishii Yoshinari (Diamet Corporation (DM), Niigata, Japan) ,  Nunomura Norio (University of Toyama, Information Technology Center, Toyama, Japan) ,  Hatakeyama Masahiko (University of Toyama, Graduate School of Science and Engineering for Research, Toyama, Japan)
資料名： Materials Science Forum  (Materials Science Forum)
巻： 941  ページ： 1734-1742  発行年： 2019年 
JST資料番号： D0716B  ISSN： 0255-5476  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： Nickelを添加した銅合金は高い耐食性を示した。したがって,それらは一般的に低品質燃料の環境で使用されている。しかし,最近のNickel消費の増加により,銅合金中のNi量を減少させることが期待されている。本研究ではNickelの含有量が異なる5種類の焼結材料試料を用いて,Ni含有量が耐食性に及ぼす影響を定量的に調べた。これらの試料を開回路電位,陽極及び陰極分極曲線測定の実験に用いた。低品質燃料における環境をシミュレートするために,0.5M Na_2S+0.1M NaOH(pH=13.05)の溶液を用いた。開回路電位の実験は,Nickelの含有量が42mass%未満のサンプルが,エアレーションの間,サンプルの表面に不動態化フィルムを形成したことを示している。分極曲線測定の実験は,各試料が基本的に陽極領域におけるCuの電位-pHダイアグラムに対応する不動態化膜形成の挙動を暗示することを示した。さらに,36.4mass%Nickelは著しく耐食性を改善した。Copyright 2019 Trans Tech Publications Ltd. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 不動態化 ,  *品質 ,  不動態皮膜 ,  アノード ,  銅合金 ,  *銅 ,  電極電位 ,  エアレーション ,  *ニッケル ,  電位 ,  曲線 ,  *耐食性 ,  分極曲線 ,  陰極分極 ,  改変 ,  化成皮膜
準シソーラス用語： 陰分極 , 【Automatic Indexing@JST】

著者キーワード (4件)： 腐食 ,  焼結合金 ,  ニッケル ,  銅

分類 (2件)： 腐食  (WB03030B) ,  腐食基礎理論,腐食試験  (WB03020Q)

タイトルに関連する用語 (7件)： 燃料 ,  Cu ,  Ni ,  Sn ,  焼結合金 ,  耐食性 ,  含有量