異なるドーピングレベルのYb:Y_3ScAl_4O_12透明セラミックの作製,微細構造および光学特性【JST・京大機械翻訳】

Fabrication, microstructure, and optical properties of Yb:Y₃ScAl₄O₁₂ transparent ceramics with different doping levels

著者 (19件)： Feng Yagang (Key Laboratory of Transparent Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, China) ,  Feng Yagang (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing, China) ,  Toci Guido (Istituto Nazionale di Ottica, Consiglio Nazionale delle Ricerche, CNR-INO, Sesto Fiorentino (Fi), Italy) ,  Pirri Angela (Istituto di Fisica Applicata “Carrara”, Consiglio Nazionale delle Ricerche, CNR-IFAC, Sesto Fiorentino (Fi), Italy) ,  Patrizi Barbara (Istituto Nazionale di Ottica, Consiglio Nazionale delle Ricerche, CNR-INO, Pisa (Pi), Italy) ,  Hu Zewang (Key Laboratory of Transparent Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, China) ,  Hu Zewang (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing, China) ,  Wei Jiabei (Key Laboratory of Transparent Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, China) ,  Wei Jiabei (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing, China) ,  Pan Hongming (Key Laboratory of Transparent Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, China) ,  Pan Hongming (School of Material Science and Engineering, Jiangsu University, Zhenjiang, China) ,  Zhang Xing (Key Laboratory of Transparent Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, China) ,  Zhang Xing (School of Material Science and Engineering, Jiangsu University, Zhenjiang, China) ,  Li Xiaoying (Key Laboratory of Transparent Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, China) ,  Li Xiaoying (School of Material Science and Engineering, Jiangsu University, Zhenjiang, China) ,  Su Sha (Key Laboratory of Transparent Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, China) ,  Su Sha (School of Material Science and Engineering, Jiangsu University, Zhenjiang, China) ,  Vannini Matteo (Istituto Nazionale di Ottica, Consiglio Nazionale delle Ricerche, CNR-INO, Sesto Fiorentino (Fi), Italy) ,  Li Jiang (Key Laboratory of Transparent Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, China)
資料名： Journal of the American Ceramic Society  (Journal of the American Ceramic Society)
巻： 103  号： 1  ページ： 224-234  発行年： 2020年 
JST資料番号： C0253A  ISSN： 0002-7820  CODEN： JACTAW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 5,10,15,20at.%の異なるイッテルビウムドーピング濃度を持つ透明Yb:Y_3ScAl_4O_12(Yb:YSAG)セラミックを固相反応焼結により成功裏に作製した。得られた全てのセラミックは,1820°Cで30時間焼結後,高密度で均一な構造を示し,200MPaの圧力で1750°C,3時間の熱間静水圧プレスによる後処理を行った。セラミックの微細構造と光学的性質に及ぼすYb3+ドーピング濃度の影響を系統的に解析した。厚さ3.2mmの10at%Yb:Y_3ScAl_4O_12セラミックは1100nmで80.9%の高い透明度を示した。10at%Yb:YSAGセラミックのレーザ放射を試験し,準連続波ポンプ条件下で最大スロープ効率67.6%,最大出力パワー11.3Wを得た。同調範囲は990から1071nmに及んだ。Copyright 2019 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 固相 ,  *セラミック ,  連続波 ,  反応焼結 ,  透明度 ,  後処理 ,  焼結 ,  レーザビーム ,  イッテルビウム ,  *微細構造 ,  *ドーピング ,  HIP【ホットプレス】
準シソーラス用語： 最大出力 ,  スロープ効率 ,  高密度 , 【Automatic Indexing@JST】

著者キーワード (4件)： 光学的性質 ,  透明セラミックス ,  Yb:Y3ScAl4O12(Yb:YSAG) ,  イッテルビウム濃度

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (6件)： ドーピング ,  Yb ,  セラミック ,  作製 ,  微細構造 ,  光学特性