磁場下のホイスラー化合物Fe_3-xMn_xSi(x=1.6,1.7,1.8)の輸送特性【JST・京大機械翻訳】

Transport properties of Heusler compounds Fe_3-xMn_xSi (x = 1.6, 1.7 and 1.8) under magnetic fields

著者 (5件)： Kato Ryota (Department of Physics and Astronomy, Graduate School of Science and Engineering, Kagoshima University, Kagoshima 890-0065, Japan) ,  Nonoyama Tomohito (Department of Physics and Astronomy, Graduate School of Science and Engineering, Kagoshima University, Kagoshima 890-0065, Japan) ,  Ooka Ryutaro (Department of Physics and Astronomy, Graduate School of Science and Engineering, Kagoshima University, Kagoshima 890-0065, Japan) ,  Shigeta Iduru (Department of Physics and Astronomy, Graduate School of Science and Engineering, Kagoshima University, Kagoshima 890-0065, Japan) ,  Hiroi Masahiko (Department of Physics and Astronomy, Graduate School of Science and Engineering, Kagoshima University, Kagoshima 890-0065, Japan)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 8  号： 11  ページ： 115019-115019-4  発行年： 2018年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 磁場下でのFe_3-xMn_xSi(x=1.6,1.7,および1.8)の輸送特性を調べるために,電気抵抗率,磁気抵抗(MR)およびHall効果の測定を行った。Fe_2MnSiは,T_Cで強磁性転移を示し,AF相と呼ばれる相への低温(T_A)で反強磁性転移を示すことが知られている。Fe_1.3mN_1.7Siに関する最近の研究はT_A以下の温度でもう一つの反強磁性転移を見出した。これはT_A2と定義され,AF_2相と呼ばれる相になる。この研究では,x=1.7と1.8のMR測定において,磁場によるMRの変化は,ある磁場で正から負へ転移することが分かった。これらの結果を磁化測定の結果と比較して,これらの点はAF2-AF遷移に対応する。結果は,これらの遷移がx=1.7よりもx=1.8に対して高い場で起こることも示した。Hall効果測定は,自発磁化が存在する温度領域でx=1.6と1.7に対して異常Hall効果を示したが,x=1.8ではなく,強磁性状態が存在しないように見えた。これらの結果は磁化測定と一致した。Copyright 2019 AIP Publishing LLC All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 電気抵抗率 ,  低温 ,  強磁性 ,  磁気抵抗 ,  異常Hall効果 ,  Hall効果 ,  磁化特性測定 ,  *磁場 ,  自発磁化
準シソーラス用語： 温度範囲 ,  反強磁性転移 ,  強磁性転移 ,  *輸送特性 , 【Automatic Indexing@JST】

分類 (1件)： 金属結晶の磁性  (BM06040T)

タイトルに関連する用語 (3件)： 磁場 ,  ホイスラー化合物 ,  輸送特性