Ta析出物で強化した3D印刷Zr基BMG複合材料の機械的性質の強化【JST・京大機械翻訳】

Enhanced mechanical properties of 3D printed Zr-based BMG composite reinforced with Ta precipitates

著者 (3件)： Zhang Pengcheng (State Key Laboratory of Material Processing and Die & Mould Technology and School of Materials Science and Engineering, Huazhong University of Science and Technology, 430074, Wuhan, China) ,  Ouyang Di (State Key Laboratory of Material Processing and Die & Mould Technology and School of Materials Science and Engineering, Huazhong University of Science and Technology, 430074, Wuhan, China) ,  Liu Lin (State Key Laboratory of Material Processing and Die & Mould Technology and School of Materials Science and Engineering, Huazhong University of Science and Technology, 430074, Wuhan, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 803  ページ： 476-483  発行年： 2019年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 選択的レーザ融解(SLM)に基づく3D印刷技術は,複雑なバルク金属ガラス(BMG)成分を作製するための新しいアプローチを提供する。しかしながら,繰返しレーザ走査によって引き起こされた熱影響部(HAZ)におけるプレ形成非晶質相の構造緩和と部分結晶化は,機械的性質,すなわち塑性と破壊靱性を低下させる。ここでは,SLM法によるTa粒子の析出で強化されたZr基金属ガラス複合材料の調製を試みた。その結果,広い範囲のエネルギー密度において,3D印刷BMG複合材料は,高い非晶質分率(>90%)と良好な機械的性質を示し,破壊強度は1.9GPa,塑性歪は約2.15%,破壊靭性(Kq)は60MPa m~1/2であり,塑性歪は3D印刷BMGsで達成された。HAZs中の非晶質相の結晶化の抑制と非晶質マトリックス中のTa粒子の析出は,高強度を維持しながら塑性と破壊靭性の強化を説明できる。本研究は,3D印刷技術を用いることによる強靭化BMG複合材料の調製のためのヒントを提供する。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 塑性歪 ,  レーザ融解 ,  エネルギー密度 ,  *タンタル ,  *複合材料 ,  破壊強さ ,  塑性 ,  破壊靱性 ,  *ジルコニウム ,  *析出物 ,  結晶化 ,  バルク金属ガラス ,  非晶質
準シソーラス用語： 強靱化 ,  *三次元印刷 , 【Automatic Indexing@JST】

著者キーワード (4件)： 選択的レーザ融解 ,  バルク金属ガラス複合材料 ,  Ta析出物 ,  破壊靱性

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (8件)： Ta ,  析出物 ,  強化 ,  3D印刷 ,  Zr ,  BMG ,  複合材料 ,  機械的性質