超超臨界回転子鋼の100mm厚異種溶接からの異なる溶接部材料の230°Cにおけるミクロ組織特性と低サイクル疲労特性【JST・京大機械翻訳】

Microstructural characteristics and low cycle fatigue properties at 230 °C of different weld zone materials from a 100 mm thick dissimilar weld of ultra-supercritical rotor steel

著者 (6件)： Long Jian (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China) ,  Zhang Lin-Jie (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China) ,  Zhang Qun-Bing (School of Materials Engineering, Xi’an Aeronautical University, Xi’an 710077, China) ,  Wang Wen-Ke (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China) ,  Zhong Jie (Dongfang Steam Turbine Limited Company, Deyang 618000, China) ,  Zhang Jian-Xun (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China)
資料名： International Journal of Fatigue  (International Journal of Fatigue)
巻： 130  ページ： Null  発行年： 2020年 
JST資料番号： D0802B  ISSN： 0142-1123  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 230°Cにおける低サイクル疲れ特性と超臨界回転子鋼製の100mm厚異種継手の異なる領域における材料の微細構造を研究した。微細構造,破壊経路および疲労破面を,走査電子顕微鏡および透過型電子顕微鏡によって特性化した。230°Cでの30Cr1Mo1V(BM-1),溶接シーム(SAW)および30Cr2Ni4MoV(BM-2)の歪レベルと疲れ寿命の間の関係をそれぞれ得た。230°Cでの低サイクル疲れ性能に及ぼす微細構造特性の影響を,疲労試料中の転位セルの形態に基づいて検討した。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： キャラクタリゼーション ,  走査電子顕微鏡 ,  微細構造 ,  *超臨界 ,  *低サイクル疲れ ,  *鋼 ,  破面 ,  電子顕微鏡観察 ,  *溶接 ,  *溶接材料 ,  疲れ寿命 ,  透過型電子顕微鏡
準シソーラス用語： 転位セル ,  溶接シーム , 【Automatic Indexing@JST】

著者キーワード (5件)： 溶接継手 ,  低サイクル疲労 ,  CrMo鋼 ,  厚い壁 ,  ロータ

分類 (1件)： 金属材料  (HC05020S)

タイトルに関連する用語 (7件)： 超臨界 ,  回転子 ,  厚 ,  溶接 ,  溶接部材 ,  組織特性 ,  低サイクル疲労