磁気測定を用いた改良9Cr-1Mo鋼のクリープ劣化のキャラクタリゼーション【JST・京大機械翻訳】

Characterization of Creep Degradation of Modified 9Cr-1Mo Steel Using Magnetic Measurement

著者 (5件)： Zhu Lin (School of Chemical Engineering, Northwest University, 229 Taibai Rd., Xi’an , China, https://orcid.org/0000-0002-0690-2596 (L.Z)) ,  Liu Xinbao (School of Chemical Engineering, Northwest University, 229 Taibai Rd., Xi’an , China (Corresponding author), e-mail:) ,  Fan Ping (School of Information Science and Technology, Northwest University, 229 Taibai Rd., Xi’an , China) ,  Yang Changlin (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, 127 West Youyi Rd., Xi’an, , China) ,  Liu Jianqiu (School of Chemical Engineering, Northwest University, 229 Taibai Rd., Xi’an , China, https://orcid.org/0000-0002-0690-2596 (L.Z))
資料名： Journal of Testing and Evaluation  (Journal of Testing and Evaluation)
巻： 48  号： 5  ページ： Null  発行年： 2020年 
JST資料番号： B0721B  ISSN： 0090-3973  CODEN： JTEVAB  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 改良9Cr-1Mo耐熱鋼のクリープ中のミクロ組織変化を,893K(620°C)での磁気ヒステリシスループ(MHL)法の非破壊法により特性化した。保磁力と残留磁気の2つのパラメータを導入して,中断したクリープ試験片の磁気特性を評価した。実験結果は,両方のパラメータが転位,析出物および微小亀裂のような微細構造に著しく敏感であることを示唆した。一次および二次クリープ段階の間,保磁力および残留磁気は,クリープ時間とともに増加し,それは,主に,析出物のピン止め転位および数密度の増加に起因した。しかし,M_23C_6炭化物の粗大化と非磁性析出物と微小亀裂によって誘起された反磁場の存在のために,保磁力と残留磁気は三次クリープ段階の間に減少した。それは,MHL技術が耐熱鋼のクリープ劣化の間,微細構造進展を評価するために大きな可能性を持つことを示唆した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *キャラクタリゼーション ,  *鋼 ,  クリープ試験 ,  微細構造 ,  磁気ヒステリシス ,  残留磁化 ,  パラメータ ,  *クリープ ,  ピン止め ,  微小亀裂 ,  炭化物 ,  析出物 ,  耐熱鋼 ,  保磁力
準シソーラス用語： 反磁場 , 【Automatic Indexing@JST】

著者キーワード (4件)： クリープ ,  微細構造 ,  磁気測定 ,  マルテンサイト鋼

分類 (2件)： 金属材料  (HC06020Z) ,  その他の材料  (HC06050G)

タイトルに関連する用語 (4件)： 磁気測定 ,  9Cr-1Mo鋼 ,  クリープ ,  キャラクタリゼーション