シェールガス工業用の環境に優しい腐食抑制剤としてのアラビアゴムを用いたCO_2飽和塩化物(KCl)溶液中のパイプライン炭素鋼(N80)の腐食抑制【JST・京大機械翻訳】

Corrosion Inhibition of Pipeline Carbon Steel (N80) in CO2-Saturated Chloride (0.5 M of KCl) Solution Using Gum Arabic as a Possible Environmentally Friendly Corrosion Inhibitor for Shale Gas Industry

著者 (3件)： Palumbo Gaetano (Department of Chemistry and Corrosion of Metals, Faculty of Foundry Engineering, AGH University of Science and Technology, Krakow, Poland) ,  Gorny Marcin (Department of Cast Alloys and Composites Engineering, Faculty of Foundry Engineering, AGH University of Science and Technology, Krakow, Poland) ,  Banas Jacek (Department of Chemistry and Corrosion of Metals, Faculty of Foundry Engineering, AGH University of Science and Technology, Krakow, Poland)
資料名： Journal of Materials Engineering and Performance  (Journal of Materials Engineering and Performance)
巻： 28  号： 10  ページ： 6458-6470  発行年： 2019年 
JST資料番号： C0161B  ISSN： 1059-9495  CODEN： JMEPEG  資料種別： 逐次刊行物 (A)
記事区分： 文献レビュー  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： アラビアゴム(GA)の阻害効果を重量損失測定と電気化学技術を用いて調べた。結果は,GAの抑制効率が抑制剤の濃度の増加とともに増加したが,温度とともに減少したことを示した。浸漬時間は抑制剤の腐食抑制性能に大きな影響を及ぼすことが分かった。分極測定は,GAが混合型抑制剤であり,陽極反応に対してより高い影響を持つことを明らかにした。抑制剤はTemkinの吸着等温式に従い,標準自由吸着エネルギーの値は混合型吸着を示し,物理吸着はより支配的であった。SEM-EDSとFT-IR測定を用いて,この知見を支持した。Copyright 2019 The Author(s) Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 吸着等温式 ,  物理吸着 ,  *塩化物 ,  *腐食抑制剤 ,  *腐食抑制作用 ,  *炭素鋼 ,  吸着 ,  *アラビアゴム ,  重量損失 ,  電気化学 ,  耐食性 ,  *抑制剤 ,  吸着エネルギー ,  分極
準シソーラス用語： 浸漬時間 , 【Automatic Indexing@JST】

著者キーワード (3件)： 二酸化炭素腐食 ,  腐食抑制 ,  アラビアゴム