市販純度アルミニウムの微細構造の進展に及ぼす室温での多軸圧縮速度の影響【JST・京大機械翻訳】

Effect of the Rate of Multiaxial Compression at Room Temperature on the Evolution of Microstructure of Commercial-Purity Aluminum

著者 (6件)： Yang Y. (School of Material Science and Engineering, Central South University, Changsha, China) ,  Yang Y. (Institute of Fluid Physics, China Academy of Engineering Physics, Mianyang, China) ,  Yang Y. (Key Laboratory of the Ministry of Education for Nonferrous Metal Materials Science and Engineering, Central South University, Changsha, China) ,  Yang S. J. (School of Material Science and Engineering, Central South University, Changsha, China) ,  Wang Z. (School of Material Science and Engineering, Central South University, Changsha, China) ,  Gao X. F. (School of Material Science and Engineering, Central South University, Changsha, China)
資料名： Metal Science and Heat Treatment  (Metal Science and Heat Treatment)
巻： 61  号： 1-2  ページ： 96-100  発行年： 2019年 
JST資料番号： W1070A  ISSN： 0026-0673  CODEN： MHTRAN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 1.2×10~3~1.0×10~3sec-1の変形速度で室温で一軸または多軸圧縮により得られたグレード1050の商用純度アルミニウムを研究した。1パス当たりの真の歪は一定に保たれ,一方,全歪は一軸変形で1.6,多軸変形で3.0になる。透過型電子顕微鏡を用いて微細構造を決定した。高速変形は転位密度の上昇と動的回復の抑制により構造を微細化するのに最も効果的であることを示した。Copyright 2019 Springer Science+Business Media, LLC, part of Springer Nature Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 精密化 ,  *微細構造 ,  転位密度 ,  高速変形 ,  *多軸 ,  動的回復 ,  *アルミニウム ,  透過型電子顕微鏡 ,  結晶粒微細化 ,  *純度 ,  一軸 ,  歪速度
準シソーラス用語： *軸圧縮 ,  変形速度 ,  *圧縮速度 , 【Automatic Indexing@JST】

著者キーワード (5件)： 歪速度 ,  アルミニウム ,  多軸圧縮 ,  結晶粒微細化 ,  転位構造