熱間圧延プロセス中の形状と平坦性に及ぼす電気鋼のストリップ端温度降下の影響【JST・京大機械翻訳】

Effect of strip edge temperature drop of electrical steel on profile and flatness during hot rolling process

著者 (6件)： Li Yanlin (School of Mechanical Engineering, University of Science & Technology Beijing, Beijing, China) ,  Cao Jianguo (School of Mechanical Engineering, University of Science & Technology Beijing, Beijing, China) ,  Qiu Lan (School of Mechanical Engineering, University of Science & Technology Beijing, Beijing, China) ,  Kong Ning (School of Mechanical Engineering, University of Science & Technology Beijing, Beijing, China) ,  He Anrui (National Engineering Research Center of Flat Rolling Equipment, University of Science & Technology Beijing, Beijing, China) ,  Zhou Yizhong (Wuhan Iron and Steel Company Ltd., China Baowu Steel Group Corporation, Wuhan, Hubei, China)
資料名： Advances in Mechanical Engineering  (Advances in Mechanical Engineering)
巻： 11  号： 4  ページ： 1687814019840471  発行年： 2019年 
JST資料番号： W5122A  ISSN： 1687-8140  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本論文の目的は,熱間圧延プロセスの間の高温相転移によって引き起こされた電気的鋼ストリップの不均一変形問題を解明することである。電気的鋼ストリップの熱間圧延プロセスをABAQUSソフトウェアによって築き上げて,電気的鋼の構成モデルをインポートした。ストリップの輪郭と平坦性に及ぼす電気的鋼ストリップの端部における温度降下の影響を研究した。シミュレーション結果により,ストリップ端部温度降下は,電気鋼板の熱間圧延プロセスに,大きな影響を及ぼした。電気的鋼ストリップが単相状態にあるとき,ストリップ端部温度降下は,ストリップクラウンを減少することができた。しかし,さらに,ストリップ端部においてより大きな圧延圧力と局所的高いポイント高さに導いた。電気的鋼ストリップが二相状態にあるとき,ストリップ端部における局所的高点高さは存在しないが,しかし,ストリップ端部温度降下は,より大きなストリップクラウンに導くことができた。Copyright The Author(s) 2019 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： シミュレーション ,  ソフトウェア ,  高温 ,  相転移 ,  *鋼 ,  構成モデル ,  *帯板 ,  有限要素法 ,  *圧延 ,  単相 ,  *熱間圧延 ,  *平坦性 ,  帯鋼
準シソーラス用語： クラウン ,  ABAQUS , 【Automatic Indexing@JST】

著者キーワード (5件)： 電気鋼 ,  温度 ,  熱間圧延 ,  有限要素法 ,  プロファイルと平坦性制御

分類 (1件)： 圧延技術  (WC06030Z)

タイトルに関連する用語 (4件)： 熱間圧延プロセス ,  平坦性 ,  ストリップ ,  温度降下