ポリジビニルベンゼン(PDVB)の超低応力,熱安定架橋高分子膜【JST・京大機械翻訳】

Ultralow Stress, Thermally Stable Cross-Linked Polymer Films of Polydivinylbenzene (PDVB)

著者 (7件)： Lepro Xavier (Lawrence Livermore National Laboratory, P.O. Box 808, California, United States) ,  Ehrmann Paul (Lawrence Livermore National Laboratory, P.O. Box 808, California, United States) ,  Menapace Joseph (Lawrence Livermore National Laboratory, P.O. Box 808, California, United States) ,  Lotscher Johann (Lawrence Livermore National Laboratory, P.O. Box 808, California, United States) ,  Shin Swanee (Lawrence Livermore National Laboratory, P.O. Box 808, California, United States) ,  Meissner Richard (Lawrence Livermore National Laboratory, P.O. Box 808, California, United States) ,  Baxamusa Salmaan (Lawrence Livermore National Laboratory, P.O. Box 808, California, United States)
資料名： Langmuir  (Langmuir)
巻： 33  号： 21  ページ： 5204-5212  発行年： 2017年 
JST資料番号： A0231B  ISSN： 0743-7463  CODEN： LANGD5  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： ポリスチレンと密接に関連しているが,ポリ(ジビニルベンゼン)(PDVB)はその合成に関連する困難さのために限られた有用性を見出している。高架橋高分子として,PDVBは不溶性であり,溶融または溶媒ベースのプロセスによって膜に形状をほとんど形成することができない。ここでは,厚さ25μmまでのPDVBのほぼ無応力,高透明,自立膜の開始化学蒸着(iCVD)について報告する。膜は初めに引張固有応力下で成長するが,厚さと共により圧縮性になり,それらが厚さ≧10μmに達すると,最終的にゼロ応力値に収束する。初期加熱により,高分子マトリックス中に残された未反応単量体の蒸発損失は,膜中の35~45MPaの引張応力を誘起した。その後,その後の加熱サイクルは可逆応力と膜膨張挙動を誘起する。架橋度を44%と推定し,高い熱安定性(300°Cまで)と機械的剛性(Young率5.2GPa)をもたらした。高架橋と組み合わせた低応力はiCVD PDVBを過酷な環境における保護被覆の優れた候補にする。Copyright 2019 American Chemical Society All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 架橋度 ,  Young率 ,  *高分子膜 ,  形態 ,  蒸発 ,  剛性 ,  化学蒸着 ,  引張 ,  引張応力 ,  熱サイクル ,  熱安定性 ,  ポリスチレン
準シソーラス用語： 逆応力 ,  自立膜 ,  *架橋高分子 , 【Automatic Indexing@JST】