Mg-3Al-3Nd合金のミクロ組織と凝固パラメータに及ぼす冷却速度の影響【JST・京大機械翻訳】

Effect of cooling rate on the microstructure and solidification parameters of Mg-3Al-3Nd alloy

著者 (5件)： Guo Erjun (School of Materials Science and Engineering, Harbin University of Science and Technology, Harbin, China) ,  Wang Lei (School of Materials Science and Engineering, Harbin University of Science and Technology, Harbin, China) ,  Feng Yicheng (School of Materials Science and Engineering, Harbin University of Science and Technology, Harbin, China) ,  Wang Liping (School of Materials Science and Engineering, Harbin University of Science and Technology, Harbin, China) ,  Chen Yanhong (School of Materials Science and Engineering, Harbin University of Science and Technology, Harbin, China)
資料名： Journal of Thermal Analysis and Calorimetry  (Journal of Thermal Analysis and Calorimetry)
巻： 135  号： 4  ページ： 2001-2008  発行年： 2019年 
JST資料番号： H0095C  ISSN： 1388-6150  CODEN： JTHEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： Mg-3Al-3Nd合金のミクロ組織と凝固パラメータに及ぼす冷却速度の影響を熱分析によって研究した。本研究では,異なる冷却速度を選んだ。それは,0.3から3.5°Cs-1の範囲のステップ砂型によって達成された。凝固パラメータは,冷却曲線およびその一次および二次微分曲線から決定した。結果は,Mg-3Al-3Nd合金の微細構造と凝固パラメータが冷却速度の変化により影響されることを示した。核形成温度,過冷却温度,凝固温度の範囲は全て冷却速度の増加と共に増加した。Al_2NdおよびAl_11Nd_3相の析出温度,再冷却過冷却温度および全凝固時間は,全て,冷却速度の増加とともに減少した。Mg-3Al-3Nd合金の粒径は微細化し,金属間化合物相は冷却速度の増加と共により均一に分布した。さらに,金属間化合物相の体積分率とAl_2Nd粒子の数密度も冷却速度の増加と共に増加した。Copyright 2018 Akademiai Kiado, Budapest, Hungary Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  *凝固 ,  熱分析 ,  *冷却速度 ,  曲線 ,  金属間化合物 ,  体積率 ,  核形成 ,  微細構造 ,  過冷却 ,  精密化 ,  粒径 ,  *金属組織 ,  凝固点
準シソーラス用語： 冷却曲線 , 【Automatic Indexing@JST】

著者キーワード (5件)： Mg合金 ,  熱分析 ,  冷却速度 ,  凝固パラメータ ,  微細構造