鍛造した2XXX級アルミニウム粉末冶金合金のミクロ組織の進展【JST・京大機械翻訳】

Microstructural evolution of a forged 2XXX series aluminum powder metallurgy alloy

著者 (7件)： Sweet Gregory A.W. (Dalhousie University, Department of Mechanical Engineering, 1360 Barrington Street, Halifax, Nova Scotia B3J 1Z1, Canada) ,  Amirkhiz Babak Shalchi (CanmetMATERIALS, Natural Resources Canada, 183 Longwood Road South, Hamilton, Ontario L8P 0A5, Canada) ,  Williams Bruce W. (CanmetMATERIALS, Natural Resources Canada, 183 Longwood Road South, Hamilton, Ontario L8P 0A5, Canada) ,  Taylor Alan (GKN Sinter Metals, 2200 N. Opdyke Road, Auburn Hills, MI 48326, USA) ,  Hexemer Rich L. (GKN Sinter Metals, 2200 N. Opdyke Road, Auburn Hills, MI 48326, USA) ,  Donaldson Ian W. (GKN Sinter Metals, 2200 N. Opdyke Road, Auburn Hills, MI 48326, USA) ,  Bishop Donald Paul (Dalhousie University, Department of Mechanical Engineering, 1360 Barrington Street, Halifax, Nova Scotia B3J 1Z1, Canada)
資料名： Materials Characterization  (Materials Characterization)
巻： 151  ページ： 342-350  発行年： 2019年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 工業的に関連する2000シリーズアルミニウム粉末冶金合金について,熱間アッセット鍛造に対するミクロ組織応答を研究した。引張特性の発達が真の圧縮鍛造歪0mm/mmから1.55mm/mmに対して記録されたように,十分に大きな試料を作製した。完全な理論密度値が得られ,引張延性の4倍の改善が観察された。焼結T6成分の引張強さは357MPaで測定され,一方,1.40mm/mmまでの鍛造は418MPaまで増加した。微細構造強化は主にS相析出物であることが分かった。非鍛造試料の事前粒子境界(PPB)はMgOとMg_2Sn微結晶で連続的に修飾されていることが分かった。熱間鍛造試料におけるそのような境界はクラスタに離散化され,酸化物や他の二次相を欠くPPBの領域を生成した。機械的性質の改善はこの効果に大きく起因した。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  *金属組織 ,  焼結 ,  結晶粒界 ,  析出物 ,  熱間鍛造 ,  *粉末冶金 ,  延性 ,  微細構造 ,  クラスタ ,  *アルミニウム ,  引張 ,  微結晶 ,  *鍛造 ,  引張強さ

著者キーワード (6件)： アルミニウム粉末冶金 ,  鍛造 ,  機械的性質 ,  TEM ,  事前粒子境界 ,  酸素

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： 鍛造 ,  アルミニウム ,  粉末冶金 ,  合金 ,  ミクロ組織 ,  進展