伝統的熱間押出による高強度低希土類合金マグネシウム合金【JST・京大機械翻訳】

A high-strength low-rare-earth-alloyed magnesium alloy via traditional hot-extrusion

著者 (13件)： Zhang Dongdong (Key Laboratory of Automobile Materials of Ministry of Education, Department of Materials Science and Engineering, Nanling Campus, Jilin University, Changchun, 130025, China) ,  Zhang Dongdong (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, 130022, China) ,  Yang Qiang (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, 130022, China) ,  Guan Kai (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, 130022, China) ,  Li Baishun (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, 130022, China) ,  Wang Nan (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, 130022, China) ,  Qin Pengfei (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, 130022, China) ,  Jiang Bo (Key Laboratory of Automobile Materials of Ministry of Education, Department of Materials Science and Engineering, Nanling Campus, Jilin University, Changchun, 130025, China) ,  Sun Chi (Key Laboratory of Automobile Materials of Ministry of Education, Department of Materials Science and Engineering, Nanling Campus, Jilin University, Changchun, 130025, China) ,  Qin Xin (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, 130022, China) ,  Tian Zheng (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, 130022, China) ,  Cao Zhanyi (Key Laboratory of Automobile Materials of Ministry of Education, Department of Materials Science and Engineering, Nanling Campus, Jilin University, Changchun, 130025, China) ,  Meng Jian (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, 130022, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 810  ページ： Null  発行年： 2019年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 高強度低希土類合金化Mg-3.5Sm-2Yb-0.6Zn-0.4Zr合金を,熱間押出とそれに続く人工時効によるインゴット冶金プロセスにより処理した。ピーク時効試料は,高RE含有量を含む押出Mg-Gd基合金の大部分より449MPaの高い降伏強度を示し,T8処理2024Al合金のそれに匹敵した。研究した合金は典型的な二モード微細構造を示し,ランダム集合組織を持つ動的再結晶(DRXed)結晶粒と強い基底繊維集合組織を持つ粗い非再結晶領域から成っていた。加えて,破砕したMg_5ReとMg_41RE_5相は,押出ストリンガーに分布した。微細なMg_3RE粒子の豊富はDXRed領域で動的に析出し,結晶粒界ピン止めによってDRXed結晶粒成長を効果的に抑制した。非DXRed領域内では,均一に緻密なMg_3REとMg_12REナノ析出物が観察された。また,非DXRed領域において,多くの基底<a>転位およびいくつかの非基底<c+a>転位があった。その後の人工時効は,延性をわずかに低下させたが,基礎析出物を導入することにより合金の強度を著しく向上させた。最後に,超高降伏強度は,強い基底繊維集合組織,二モード微細構造,および多数の析出粒子の複合効果に起因することを明らかにした。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 析出物 ,  *合金 ,  延性 ,  動的再結晶 ,  *熱間押出 ,  *マグネシウム合金 ,  降伏強さ ,  繊維組織 ,  再結晶 ,  インゴット ,  結晶粒界 ,  結晶成長 ,  微細構造 ,  結晶粒
準シソーラス用語： ピーク時効 , 【Automatic Indexing@JST】

著者キーワード (5件)： マグネシウム合金 ,  高強度 ,  微細構造 ,  透過型電子顕微鏡(TEM) ,  押出

分類 (2件)： 機械的性質  (WB02030U) ,  押出  (WC04020A)

タイトルに関連する用語 (4件)： 熱間押出 ,  高強度 ,  希土類合金 ,  マグネシウム合金