スーパーキャパシタ電極として増強された電気化学的性能に向けた多孔質CoOナノウォールの形態調整【JST・京大機械翻訳】

Morphology tuning of porous CoO nanowall towards enhanced electrochemical performance as supercapacitors electrodes

著者 (7件)： Tang Ning (School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Wang Wei (School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  You Huihui (School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Zhai Zhangjie (School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Hilario Jonas (School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Zeng Liang (School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Zhang Lei (School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China)
資料名： Catalysis Today  (Catalysis Today)
巻： 330  ページ： 240-245  発行年： 2019年 
JST資料番号： T0363A  ISSN： 0920-5861  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 多孔質ナノウォール構造を有するCoOを,ソルボサーマルとアニーリングの組合せプロセスにより作製した。CoOの微細形態は,アニーリング温度を制御することによって微調整される。約50nm以下のナノサイズの細孔が,65m~2g(-1)の高い比表面積を有する400°Cのアニーリングで達成された。独特の多孔質ナノウォール構造は大きな表面積をもたらし,電解質/電極界面を増加させ,CoOの電気化学的性能を向上させた。1Ag~(-1)の高い比静電容量(1~20Ag~(-1))と良好なサイクル安定性(5000サイクル後の初期静電容量の92.9%)が得られ,スーパーキャパシタ用の有望な電極となった。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 多孔質体 ,  比表面積 ,  表面積 ,  細孔 ,  *電力コンデンサ ,  静電容量 ,  電解質 ,  *多孔性 ,  焼なまし
準シソーラス用語： サイクル安定性 ,  比静電容量 ,  電極界面 ,  微調整 ,  アニーリング温度 ,  *ナノウォール ,  *電気化学的性能 ,  *スーパーキャパシタ , 【Automatic Indexing@JST】

著者キーワード (4件)： 多孔質ナノウォール ,  スーパーキャパシタ ,  CoO ,  電気化学的性能

分類 (3件)： その他の触媒  (CB06123Z) ,  触媒の調製  (CB06110P) ,  電気化学反応  (CB07050F)

タイトルに関連する用語 (6件)： スーパーキャパシタ ,  増強 ,  電気化学的性能 ,  多孔質 ,  ナノウォール ,  形態