結晶粒界とヘテロ構造界面における熱伝導率の低減によるナノ結晶Sb_2Te_3/Cr二重層の改善された熱電性能【JST・京大機械翻訳】

Improved thermoelectric performances of nanocrystalline Sb₂Te₃/Cr bilayers by reducing thermal conductivity in the grain boundaries and heterostructure interface

著者 (5件)： Mori Ryotaro (Department of Materials Science, Tokai University, 4-1-1 Kitakaname, Hiratsuka, Kanagawa 259-1292, Japan) ,  Kurokawa Takuya (Department of Materials Science, Tokai University, 4-1-1 Kitakaname, Hiratsuka, Kanagawa 259-1292, Japan) ,  Yamauchi Kazuki (Department of Materials Science, Tokai University, 4-1-1 Kitakaname, Hiratsuka, Kanagawa 259-1292, Japan) ,  Tanaka Saburo (Department of Mechanical Engineering, College of Engineering, Nihon University, 1 Nakagawara, Tokusada, Tamuramachi, Koriyama, Fukushima 963-8642, Japan) ,  Takashiri Masayuki (Department of Materials Science, Tokai University, 4-1-1 Kitakaname, Hiratsuka, Kanagawa 259-1292, Japan)
資料名： Vacuum  (Vacuum)
巻： 161  ページ： 92-97  発行年： 2019年 
JST資料番号： E0347A  ISSN： 0042-207X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 種々のCr層厚を有するナノ結晶Sb_2Te_3/Cr二層を,熱電性能を改善する目的で調製した。Sb_2Te_3膜の堆積前に,厚さが0~116nmのCr層をガラス基板上に堆積した。Sb_2Te_3/Cr二層の断面形態は,Cr層がSb_2Te_3膜と基板の両方に密接に結合していることを示した。単一Sb_2Te_3膜に対して,9.1μW/(cm K2)の最高力率を得た。一方,0.75W/(m K)の最低熱伝導率(3ω法を用いて測定)を,73nmのCr層厚をもつSb_2Te_3/Cr二層に対して記録した。これは,ナノ結晶Sb_2Te_3膜の結晶粒界上のフォノン散乱とSb_2Te_3膜とCr層の間のヘテロ構造界面の複合フォノン散乱に起因した。最高性能指数(ZT=0.28)はSb_2Te_3/Cr二層(Cr=73nm)で達成され,一方,単一Sb_2Te_3膜は0.11のZTを与えた。ナノ結晶Sb_2Te_3/Cr二層の熱電性能は,適切な厚さのCr層を導入することにより改善できると結論した。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *結晶粒界 ,  *ナノ結晶 ,  層厚 ,  形態 ,  *熱伝導率 ,  *クロム ,  基板 ,  性能指数 ,  *界面 ,  フォノン散乱 ,  3ω法 ,  ガラス基板 ,  二層 ,  *二重層 ,  *ヘテロ構造

著者キーワード (5件)： 熱電性能 ,  ナノ結晶Sb_2Te_3/Cr二重層 ,  熱伝導率 ,  粒界 ,  ヘテロ構造界面

分類 (2件)： 半導体薄膜  (BK14040E) ,  固相転移  (BL04020G)

タイトルに関連する用語 (7件)： 結晶粒界 ,  ヘテロ構造 ,  界面 ,  熱伝導率 ,  ナノ結晶 ,  Cr ,  重層