Taguchi法によるNiAl/Cr2C3被覆の熱溶射パラメータの最適化【JST・京大機械翻訳】

Optimization of Thermal Spray Parameters of NiAl/Cr2C3 Coating by Taguchi Method

著者 (5件)： Tahari M. (Esfarayen University of Technology, Engineering Department North Khorasan Iran) ,  Luo B. (Xi’an Jiaotong University, International Research Center for Renewable Energy, State Key Laboratory of Multiphase Flow in Power Engineering Xi’an China) ,  Geng J. (Xi’an Jiaotong University, International Research Center for Renewable Energy, State Key Laboratory of Multiphase Flow in Power Engineering Xi’an China) ,  Jing D. (Xi’an Jiaotong University, International Research Center for Renewable Energy, State Key Laboratory of Multiphase Flow in Power Engineering Xi’an China) ,  Hatami M. (Esfarayen University of Technology, Engineering Department North Khorasan Iran)
資料名： Solid State Phenomena  (Solid State Phenomena)
巻： 295  ページ： 9-14  発行年： 2019年 
JST資料番号： T0583A  ISSN： 1012-0394  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： 本研究では,NiAl/Cr2C3溶射皮膜の耐摩耗性に及ぼす溶射過程の影響を調べた。この目的のために,NiAlパワーを10%wtと混合した。Cr2C3粉末をアルゴン雰囲気で1時間粉砕した。電圧(V),電流(A),噴霧距離(mm),粉末供給速度(gr/min)などのAPSパラメータを応答曲面法を用いて最適化した。被覆の品質に及ぼすスプレーパラメータの調査効果に関して,SEMとピンで分析したコーティングの多孔性と耐摩耗性を,ディスク摩耗試験で分析した。結果は,電圧と電流の増加がより効果的な他のパラメータであることを示した。粉末供給速度と噴霧距離の増加は,被覆の空隙率を集中的に増加させた。Copyright 2019 Trans Tech Publications Ltd. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 品質 ,  噴霧 ,  電流 ,  耐摩耗性 ,  *溶射 ,  摩耗試験 ,  電圧 ,  *最適化 ,  応答曲面法 ,  粉体 ,  空隙率 ,  円板 ,  多孔性 ,  溶射層 ,  *被覆

著者キーワード (4件)： NiAl ,  APS ,  田口 ,  耐摩耗性

分類 (3件)： セラミック・磁器の性質  (YC03030G) ,  セラミック・陶磁器の製造  (YC03020V) ,  繊維強化金属  (WE04040C)

タイトルに関連する用語 (3件)： 熱溶射 ,  パラメータ ,  最適化