NiCrMoV鋼溶接継手の定荷重試験における破壊位置遷移【JST・京大機械翻訳】

Fracture location transition in constant load tests of a NiCrMoV steel welded joint

著者 (5件)： Weng Shuo (School of Mechanical Engineering, University of Shanghai for Science and Technology, Shanghai 200093, China) ,  Huang Yuhui (School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai 200237, China) ,  Xuan Fuzhen (School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai 200237, China) ,  Zheng Songlin (School of Mechanical Engineering, University of Shanghai for Science and Technology, Shanghai 200093, China) ,  Zheng Songlin (Machinery Industry Key Laboratory for Mechanical Strength and Reliability Evaluation of Auto Chassis Components, University of Shanghai for Science and Technology, Shanghai 200093, China)
資料名： Materials & Design  (Materials & Design)
巻： 181  ページ： Null  発行年： 2019年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 異なる引張荷重により誘起されたNiCrMoV鋼溶接継手の破壊位置遷移を,180°C,3.5wt%NaCl中での定荷重試験により調べた。溶接継手における異なるゾーンの機械的性質を,室温での空気中での硬度測定と局所化引張試験により測定した。腐食特性を動電位分極曲線試験と走査振動電極法(SVET)試験によって特性化した。結果は,最も敏感な腐食域と最も弱い強度域が溶接継手の同じ領域に位置しないことを明らかにした。この不整合は,一定荷重試験における適用荷重による溶接継手の破壊位置をもたらす。765MPa以上の負荷荷重に対して,破壊断面はその最も弱い強度のためにWMの中央に位置する。しかし,破壊位置は760MPa以下の負荷荷重に対して溶融域にシフトし,これはガルバニと応力支援腐食の組合せ効果下でのピットに起因する応力腐食割れ(SCC)に起因する。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 引張荷重 ,  塩化ナトリウム ,  応力腐食割れ ,  *鋼 ,  *溶接継手 ,  引張試験 ,  不整合 ,  機械的性質 ,  キャラクタリゼーション ,  腐食
準シソーラス用語： 動電位分極 ,  腐食挙動 ,  局在化 ,  硬さ測定 ,  *荷重試験 , 【Automatic Indexing@JST】

著者キーワード (3件)： 溶接継手 ,  定荷重試験 ,  破壊位置遷移

分類 (2件)： 溶接部  (WC07100I) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： 溶接継手 ,  荷重試験 ,  破壊 ,  遷移