電場環境におけるセメント系材料のTSA劣化過程【JST・京大機械翻訳】

The TSA degradation process of cement-based materials in the electrical field environment

著者 (6件)： Luo Yaoling (College of Materials Science and Engineering, Chongqing University, Chongqing, 400045, China) ,  Luo Yaoling (China West Construction Group Co., Ltd., Chengdu, 610015, China) ,  Wang Chong (College of Materials Science and Engineering, Chongqing University, Chongqing, 400045, China) ,  Fang Zheng (College of Materials Science and Engineering, Chongqing University, Chongqing, 400045, China) ,  Xiao Lujun (College of Materials Science and Engineering, Chongqing University, Chongqing, 400045, China) ,  Zeng Qianpu (College of Materials Science and Engineering, Chongqing University, Chongqing, 400045, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 206  ページ： 703-716  発行年： 2019年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： セメント系材料の硫酸塩攻撃(TSA)のソーマサイト形は複雑な分解過程である。しかし,電場環境におけるTSA分解過程に関する詳細な研究はない。X線回折(XRD),Fourier変換赤外分光法(FTIR),Raman分光法(Raman)および化学分析を用いて,本研究に基づいてTSA分解過程を研究した。結果は,電場陰極Na_2SO_4溶液-陽極MgSO_4溶液群の分解過程がNa_2SO_4とMgSO_4溶液の完全浸漬に類似していることを示した。主な差異は分解速度であった。電場はTSA分解過程を明らかに加速できる。分解は試料の中心に進行し,パルプの量は120日の電場群で見られた。MgSO_4完全浸漬の分解の程度は,360日でサンプルの表面だけに影響した。MgSO_4完全浸漬の分解度は,360日で最低であった。一方,XRD,化学分析データ,および外観を組み合わせて,分解則を,パルプ(硫酸塩攻撃の代表的なソーマサイト形)を生成するための固定範囲があるとまとめ,pHとCa/Sは以下の条件を満たす必要がある:10.6<pH<11.8と4.0<Ca/S<6.4。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： アノード ,  *電場 ,  カルシウム ,  FTIR分光法 ,  硫酸塩 ,  X線回折 ,  浸漬 ,  パルプ ,  カソード ,  Raman分光法 ,  X線回折分析 ,  化学分析
準シソーラス用語： 分解速度 ,  分解過程 ,  ソーマス石 ,  セメント系材料 , 【Automatic Indexing@JST】

著者キーワード (4件)： 電場 ,  TSA ,  セメント系材料 ,  劣化プロセス

分類 (1件)： モルタル,コンクリート  (RA06042H)

タイトルに関連する用語 (5件)： 電場 ,  環境 ,  セメント系材料 ,  TSA ,  劣化過程