無マトリックス高分子ナノ複合材料熱可塑性エラストマ【JST・京大機械翻訳】

Matrix-Free Polymer Nanocomposite Thermoplastic Elastomers

著者 (6件)： Huang Yucheng (Department of Chemistry and Biochemistry, University of South Carolina, South Carolina, United States) ,  Zheng Yang (Department of Chemistry and Biochemistry, University of South Carolina, South Carolina, United States) ,  Sarkar Amrita (Department of Chemistry and Biochemistry, University of South Carolina, South Carolina, United States) ,  Xu Yanmei (Department of Chemistry and Biochemistry, University of South Carolina, South Carolina, United States) ,  Stefik Morgan (Department of Chemistry and Biochemistry, University of South Carolina, South Carolina, United States) ,  Benicewicz Brian C. (Department of Chemistry and Biochemistry, University of South Carolina, South Carolina, United States)
資料名： Macromolecules  (Macromolecules)
巻： 50  号： 12  ページ： 4742-4753  発行年： 2017年 
JST資料番号： B0952A  ISSN： 0024-9297  CODEN： MAMOBX  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 熱可塑性エラストマ(TPE)グラフト化ナノ粒子を,表面開始可逆的付加-フラグメンテーション連鎖移動(RAFT)重合によりシリカナノ粒子(NPs)上にブロック共重合体ポリ-(スチレン-block-(n-ブチルアクリレートをグラフト化することにより調製した。機械的性質に及ぼす高分子鎖長とグラフト密度の影響を,グラフト化NPsのみから作製した膜を用いて調べた。最大引張応力と弾性係数はPS鎖長の増加と共に増加した。小角X線散乱(SAXS),透過型電子顕微鏡(TEM),示差走査熱量測定(DSC)及び動的機械分析(DMA)を用いて,シリカNPsの分散及びマトリックスを含まないポリマーナノ複合材料中のブロック共重合体のミクロ相分離を調べた。高分子グラフト密度TPEはブロック共重合体の良好なミクロ相分離を示し,類似の高分子鎖長と組成をもつ低分子グラフト密度TPEよりも均一なシリカNP分散を示した。Copyright 2019 American Chemical Society All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 小角X線散乱 ,  電子顕微鏡観察 ,  ブロック共重合体 ,  ミクロ相分離 ,  *高分子 ,  ナノ粒子 ,  示差走査熱量測定 ,  弾性係数 ,  二酸化ケイ素 ,  透過型電子顕微鏡 ,  移植片 ,  動的機械分析 ,  重合
準シソーラス用語： 鎖長 ,  グラフト率 ,  シリカナノ粒子 , 【Automatic Indexing@JST】

分類 (3件)： 高分子固体の構造と形態学  (CG02022M) ,  高分子の立体構造  (CG02031G) ,  共重合  (CG04030D)

タイトルに関連する用語 (3件)： マトリックス ,  高分子ナノ複合材料 ,  熱可塑性エラストマ