積層欠陥を持つ高強度六方最密充填Coにおける相変態誘起塑性【JST・京大機械翻訳】

Phase transformation induced plasticity in high-strength hexagonal close packed Co with stacking faults

著者 (8件)： Su Ruizhe (School of Materials Engineering, Purdue University, West Lafayette, IN 47907, USA) ,  Neffati Dajla (Department of Mechanical Engineering, University of Houston, Houston, TX 77204, USA) ,  Cho Jaehun (School of Materials Engineering, Purdue University, West Lafayette, IN 47907, USA) ,  Li Qiang (School of Materials Engineering, Purdue University, West Lafayette, IN 47907, USA) ,  Ding Jie (School of Materials Engineering, Purdue University, West Lafayette, IN 47907, USA) ,  Wang Haiyan (School of Materials Engineering, Purdue University, West Lafayette, IN 47907, USA) ,  Kulkarni Yashashree (Department of Mechanical Engineering, University of Houston, Houston, TX 77204, USA) ,  Zhang Xinghang (School of Materials Engineering, Purdue University, West Lafayette, IN 47907, USA)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 173  ページ： 32-36  発行年： 2019年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 変形双晶と転位すべりは,六方晶最密充填(HCP)金属における二つの主要な変形機構である。ここでは,その場マイクロピラー圧縮試験により,高密度積層欠陥を有するHCP Coピラーが高い降伏強度と著しい塑性を示すことを示した。透過型電子顕微鏡研究は,変形後の広範な面心立方(FCC)Co相の形成を明らかにした。分子動力学シミュレーションにより,変形誘起相変態を確認し,既存の積層欠陥を有するHCP Coの変形機構を明らかにした。本研究は,積層欠陥と相変態によるHCP金属の高強度と塑性を達成する新しい洞察を提供する。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 降伏強さ ,  圧縮試験 ,  変形双晶 ,  *変態誘起塑性 ,  HCP金属 ,  透過型電子顕微鏡 ,  電子顕微鏡観察 ,  *塑性 ,  六方晶系 ,  *積層欠陥
準シソーラス用語： 分子動力学シミュレーション ,  マイクロピラー ,  変形機構 ,  転位すべり ,  *最密充填 ,  *高強度 , 【Automatic Indexing@JST】

著者キーワード (5件)： コバルト ,  積層欠陥 ,  ピラー圧縮 ,  相変態 ,  分子動力学シミュレーション

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： 積層欠陥 ,  高強度 ,  最密充填 ,  CO ,  変態誘起塑性