ニオブをドープしたTiO_2のルチルからアナターゼへのレーザ誘起結晶相転移【JST・京大機械翻訳】

Laser-induced crystalline phase transition from rutile to anatase of niobium doped TiO₂

著者 (6件)： Dauksta Edvins (Graduate School of Science and Technology, Shizuoka University, Hamamatsu, Shizuoka, 432-8561, Japan) ,  Medvids Arturs (Graduate School of Integrated Science and Technology, Shizuoka University, Hamamatsu, Shizuoka, 432-8561, Japan) ,  Onufrijevs Pavels (Graduate School of Integrated Science and Technology, Shizuoka University, Hamamatsu, Shizuoka, 432-8561, Japan) ,  Shimomura Masaru (Research Institute of Electronics, Shizuoka University, Hamamatsu, Shizuoka, 432-8561, Japan) ,  Fukuda Yasuo (Faculty of Materials Science and Applied Chemistry, Institute of Technical Physics, Riga Technical University, P. Valdena 3/7, Riga, LV-1048, Latvia) ,  Murakami Kenji (Research Institute of Electronics, Shizuoka University, Hamamatsu, Shizuoka, 432-8561, Japan)
資料名： Current Applied Physics  (Current Applied Physics)
巻： 19  号： 3  ページ： 351-355  発行年： 2019年 
JST資料番号： W1579A  ISSN： 1567-1739  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ニオブをドープしたTiO_2単結晶のレーザ誘起結晶相転移の研究をこの論文で議論する。TiO_2単結晶を,56MW/cm2の閾値強度で266nm nsレーザによる照射前後のRaman分光法と電子後方散乱回折を用いて研究した。実験結果はルチル単結晶からのアナターゼ相形成の証拠を示した。さらに,実験的に得られた結晶学的集合組織の解析は,変換されたTiO_2層が優先配向を有する多結晶構造を有することを示した。Raman分光法によると,アナターゼ相の量はレーザパルスの数と共に増加し,用量依存変換過程を示した。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *相転移 ,  *レーザ ,  Raman分光法 ,  優先配向 ,  *ルチル ,  集合組織 ,  *結晶 ,  多結晶 ,  単結晶 ,  *ニオブ ,  *アナターゼ ,  *ドーピング
準シソーラス用語： *結晶相 ,  二層 ,  *レーザ誘起 , 【Automatic Indexing@JST】

著者キーワード (6件)： 相転移 ,  TiO_2 ,  アナターゼ ,  ルチル ,  レーザ加工 ,  結晶相