Li_2ZrO_3を用いた表面改質によるLi_1.2Ni_0.13Mn_0.54Co_2O_2カソード材料の表面劣化と電圧減衰の緩和【JST・京大機械翻訳】

Mitigating the Surface Degradation and Voltage Decay of Li_1.2Ni_0.13Mn_0.54Co_0.13O₂ Cathode Material through Surface Modification Using Li₂ZrO₃

著者 (5件)： Prakasha Kunkanadu R. (CSIR - Network Institutes of Solar Energy (CSIR - NISE), CSIR - Central Electrochemical Research Institute-Chennai Unit) ,  Prakasha Kunkanadu R. (Academy of Scientific and Innovative Research (AcSIR), CSIR - Central Electrochemical Research Institute-Chennai Unit) ,  Sathish Marappan (Functional Materials Division, CSIR - Central Electrochemical Research Institute, India) ,  Bera Parthasarathi (Surface Engineering Division, CSIR - National Aerospace Laboratories, India) ,  Prakash Annigere S. (CSIR - Network Institutes of Solar Energy (CSIR - NISE), CSIR - Central Electrochemical Research Institute-Chennai Unit)
資料名： ACS Omega  (ACS Omega)
巻： 2  号： 5  ページ： 2308-2316  発行年： 2017年 
JST資料番号： W5044A  ISSN： 2470-1343  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： Liリッチ相に関連した表面劣化と電圧減衰の問題に取り組むために,Li_2Ni_3Mn_0.54Co_0.13O_2(LNMC)上にLi_2ZrO_3(LZO)を簡単な湿式化学プロセスにより被覆した。約10nmの厚さのLNMC上に被覆されたLZO相は,構造的完全性を提供し,充放電過程を通してイオン経路を容易にし,電気化学的性能の著しい改善をもたらす。表面修飾カソード材料は225mAhg(-1)(C/5速度で)の可逆容量を示し,100サイクル後に初期容量の85%を保持した。一方,未被覆の未処理試料は234mAhg(-1)の容量を示し,同一条件下で初期容量の57%しか保持しなかった。電気化学インピーダンス分光法は,LZO被覆がサイクル中の電極と電解質の間の界面の安定化に重要な役割を果たすことを明らかにした。したがって,それは材料劣化と電圧フェージングを緩和し,電気化学的性能を改善する。Copyright 2019 American Chemical Society All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 完全性 ,  界面 ,  被覆 ,  *電圧 ,  電解質 ,  イオン ,  電池容量 ,  充放電サイクル ,  *表面改質 ,  化学プロセス
準シソーラス用語： 材料劣化 ,  電気化学インピーダンス分光法 ,  可逆容量 ,  電気化学的性能 ,  充放電 ,  *表面劣化 ,  *カソード材料【電池】 , 【Automatic Indexing@JST】