水蒸気コーティングにより作製したアルミニウム合金シート上に形成された水酸化物膜の微細構造と亀裂挙動【JST・京大機械翻訳】

Microstructure and cracking behavior of hydroxide films formed on aluminum-alloy sheets prepared by steam coating

著者 (4件)： Li Hongmei (Department of Materials Process Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya, 464-8603, Japan) ,  Takata Naoki (Department of Materials Process Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya, 464-8603, Japan) ,  Kobashi Makoto (Department of Materials Process Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya, 464-8603, Japan) ,  Serizawa Ai (Department of Materials Science and Engineering, Shibaura Institute of Technology, Toyosu, Koto-ku, Tokyo, 135-8548, Japan)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 764  ページ： Null  発行年： 2019年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Al-Mg-Si合金(6061グレード)シート上に形成された水酸化物膜内部に伝搬する亀裂を特性化した。異なる厚さの0.7μmと1.4μmの連続水酸化物膜が,それぞれ180°Cと200°Cの異なる温度で形成された。微細構造特性化により,これらの水酸化物膜は多結晶γ-AlO(OH)層(表面側に)と連続非晶質層(Al合金側)から成る二層構造を示すことが明らかになった。曲げ試験は,引張および圧縮下で水酸化物膜内部に多数の亀裂を引き起こした。引張歪表面では,それらの層間剥離は観察されなかったが,多数の垂直亀裂が水酸化物膜を貫通した。圧縮歪表面では,上部γ-AlO(OH)層の局所的な剥離が生じた。しかし,圧縮下で変形したAl合金基板上の下部非晶質層では亀裂は観察されなかった。これらの結果は,水蒸気被覆によって調製された二重層構造水酸化物膜がAl合金基板への顕著な接着を示すことを示している。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 引張 ,  非晶質 ,  *亀裂 ,  *アルミニウム合金 ,  多結晶 ,  *酸化膜 ,  曲げ試験 ,  *合金 ,  基板 ,  接着 ,  キャラクタリゼーション ,  *微細構造 ,  *被覆 ,  圧縮歪 ,  引張歪 ,  *化成皮膜

著者キーワード (6件)： アルミニウム合金 ,  蒸気コーティング ,  微細構造 ,  水酸化物膜 ,  曲げ試験 ,  接着

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (8件)： 水蒸気 ,  コーティング ,  作製 ,  アルミニウム合金 ,  水酸化物 ,  微細構造 ,  亀裂 ,  挙動