分子ガラスの表面拡散に及ぼす水素結合の影響:3種のトリアジンの比較【JST・京大機械翻訳】

Influence of Hydrogen Bonding on the Surface Diffusion of Molecular Glasses: Comparison of Three Triazines

著者 (7件)： Chen Yinshan (School of Pharmacy, University of Wisconsin-Madison, Wisconsin, United States) ,  Zhu Men (Department of Chemistry, University of Wisconsin-Madison, Wisconsin, United States) ,  Laventure Audrey (Department of Chemistry and Chemical Engineering, Royal Military College of Canada, Ontario, Canada) ,  Lebel Olivier (Department of Chemistry and Chemical Engineering, Royal Military College of Canada, Ontario, Canada) ,  Ediger M. D. (Department of Chemistry, University of Wisconsin-Madison, Wisconsin, United States) ,  Yu Lian (School of Pharmacy, University of Wisconsin-Madison, Wisconsin, United States) ,  Yu Lian (Department of Chemistry, University of Wisconsin-Madison, Wisconsin, United States)
資料名： Journal of Physical Chemistry B  (Journal of Physical Chemistry B)
巻： 121  号： 29  ページ： 7221-7227  発行年： 2017年 
JST資料番号： W0921A  ISSN： 1520-6106  CODEN： JPCBFK  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 表面拡散に及ぼす分子間水素結合の影響を調べるために,三つの密接に関連した分子ガラスについて表面格子減衰測定を行った。3つの分子は,ビス-(3,5-ジメチル-フェニルアミノ)-1,3,5-トリアジンの誘導体であり,2-位置における官能基Rにおいてのみ異なり,RはC_2H_5,OCH_3,およびNHCH_3であり,それぞれ「Et」,「OMe」および「NHMe」と呼ばれた。3つの分子のうち,NHMeはEtおよびOMeよりもより広範な分子間水素結合を形成し,より遅い表面拡散を有することが分かった。EtとOMeについては,表面拡散は非常に速く,温度が低下すると表面格子減衰の機構として粘性流を置換する。対照的に,同じ条件下でNHMeに対してそのような転移は観察されず,著しく遅い表面拡散を示した。この結果は,広範な分子間水素結合が分子ガラスにおける表面拡散を遅くし,表面環境においてさえも水素結合の持続性に起因するという以前の発見と一致する。この結果は,EtとOMeのそれらに対するNHMeの気相蒸着ガラスの低い安定性とも一致し,表面移動度が気相堆積ガラスの安定性を制御するという見解を支持する。Copyright 2019 American Chemical Society All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】