バイオベースの層毎被覆ラミー織物強化不飽和ポリエステル樹脂複合材料の作製と特性【JST・京大機械翻訳】

Fabrication and Properties of Biobased Layer-by-Layer Coated Ramie Fabric-Reinforced Unsaturated Polyester Resin Composites

著者 (6件)： Yu Xiaojuan (State Key Laboratory of Fire Science, University of Science and Technology of China, P. R. China) ,  Pan Ying (State Key Laboratory of Fire Science, University of Science and Technology of China, P. R. China) ,  Wang Dong (State Key Laboratory of Fire Science, University of Science and Technology of China, P. R. China) ,  Yuan Bihe (School of Resources and Environmental Engineering, Wuhan University of Technology, P. R. China) ,  Song Lei (State Key Laboratory of Fire Science, University of Science and Technology of China, P. R. China) ,  Hu Yuan (State Key Laboratory of Fire Science, University of Science and Technology of China, P. R. China)
資料名： Industrial & Engineering Chemistry Research  (Industrial & Engineering Chemistry Research)
巻： 56  号： 16  ページ： 4758-4767  発行年： 2017年 
JST資料番号： C0385C  ISSN： 0888-5885  CODEN： IECRED  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： ラミー布を,二塩基電解質,すなわちカチオン性キトサンと陰イオン性フィチン酸,および層毎(LbL)集合法による難燃性陽イオン電解質メラミンで修飾した。次に,LbL改質織物強化不飽和ポリエステル樹脂(UPR)複合材料を,ハンドレイアップ法によって製造した。LbL改質布強化UPR複合材料の開始熱分解温度は,生の織物強化UPR試料のそれより低く,一方,複合材料のチャー残留物は大きく改善され,可燃性有機揮発性物質の放出は燃焼中に抑制された。さらに,複合材料の難燃性はLbL集合数の増加によって強化され,それは顕著に減少したピーク熱放出速度とコーン熱量測定試験から得られた全熱放出値によって証明された。複合材料の限界酸素指数値は26.0%から34.5%に増加した。Copyright 2019 American Chemical Society All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *コンポジットレジン ,  熱放射 ,  *複合材料 ,  揮発分 ,  キトサン ,  電解質 ,  *被覆 ,  チャー ,  カチオン ,  難燃性 ,  可燃性 ,  窒素複素環化合物 ,  糖アルコール ,  イノシトールリン酸
準シソーラス用語： 放出速度 ,  熱分解温度 , 【Automatic Indexing@JST】

分類 (1件)： 難燃剤  (YH05060Q)

物質索引 (2件)： メラミン ,  フィチン酸

タイトルに関連する用語 (7件)： 層 ,  ラミー ,  織物 ,  強化 ,  不飽和ポリエステル樹脂 ,  複合材料 ,  作製